Stacked Ge nanocrystals with ultrathin SiO₂ separation layers.

The aim of this work is the tailored growth of Ge nanocrystals (NCs) in (GeO(x)/SiO(2)) multilayers (ML) for photovoltaic applications. For this purpose the fabrication of regularly stacked Ge NCs separated by ultrathin SiO(2) layers is essential to enable charge carrier transport by direct tunnelling. In this paper we report on the fabrication of (GeO(x)/SiO(2))(50) multilayer stacks via reactive dc magnetron sputtering and Ge NCs formation after subsequent annealing. It is shown that magnetron sputtering allows us to deposit very regular ML stacks with a total thickness of about 300 nm, characterized by ultrathin (down to 1 nm) and very smooth (roughness ∼ 0.6 nm) SiO(2) separation layers. A main challenge is to keep these properties for a thermal budget necessary to form Ge NCs. For this reason, the temperature dependence of phase separation. Ge crystallization and ML morphology was investigated by Rutherford backscattering, x-ray scattering, Raman spectroscopy and electron microscopy. The formation of size confined Ge NCs of about 5 nm after annealing of only 550 °C is confirmed. This low thermal budget ensures the suppression of GeO emanation and multilayer stability. Spectroscopic ellipsometry was applied to determine the optical Ge NC bandgap to (1.65 ± 0.5) eV.