INTRODUCTION: Control of root torque is often achieved by introducing a twist in a rectangular archwire. The purpose of this study was to investigate third-order torque on different types of self-ligated brackets by analyzing the bracket's elastic and plastic deformations in conjunction with the expressed torque at varying angles of twist. METHODS: An orthodontic bracket was mounted to a load cell that measured forces and moments in all directions. The wire was twisted in the bracket via a stepper motor, controlled by custom software. Overhead images were taken by a camera through a microscope and processed by using optical correlation to measure deformation. RESULTS: At the maximum torquing angle of 63° with 0.019 × 0.025-in stainless steel wire, the total elastic and plastic deformation values were 0.063, 0.033, and 0.137 mm for Damon Q (Ormco, Orange, Calif), In-Ovation R (GAC, Bohemia, NY), and Speed (Strite Industries, Cambridge, Ontario, Canada), respectively. The total plastic deformation values were 0.015, 0.006, and 0.086 mm, respectively, measured at 0° of unloading. CONCLUSIONS: In-Ovation R had the least deformation due to torquing of the 3 investigated bracket types. Damon Q and Speed on average had approximately 2.5 and 14 times greater maximum plastic deformation, respectively, than did In-Ovation R.
INTRODUCTION: Control of root torque is often achieved by introducing a twist in a rectangular archwire. The purpose of this study was to investigate third-order torque on different types of self-ligated brackets by analyzing the bracket's elastic and plastic deformations in conjunction with the expressed torque at varying angles of twist. METHODS: An orthodontic bracket was mounted to a load cell that measured forces and moments in all directions. The wire was twisted in the bracket via a stepper motor, controlled by custom software. Overhead images were taken by a camera through a microscope and processed by using optical correlation to measure deformation. RESULTS: At the maximum torquing angle of 63° with 0.019 × 0.025-in stainless steel wire, the total elastic and plastic deformation values were 0.063, 0.033, and 0.137 mm for Damon Q (Ormco, Orange, Calif), In-Ovation R (GAC, Bohemia, NY), and Speed (Strite Industries, Cambridge, Ontario, Canada), respectively. The total plastic deformation values were 0.015, 0.006, and 0.086 mm, respectively, measured at 0° of unloading. CONCLUSIONS: In-Ovation R had the least deformation due to torquing of the 3 investigated bracket types. Damon Q and Speed on average had approximately 2.5 and 14 times greater maximum plastic deformation, respectively, than did In-Ovation R.