Growth of piezoelectric water-free GeO2 and SiO2-substituted GeO2 single-crystals.

Using the slow-cooling method in selected fluxes, we have grown spontaneously nucleated single-crystals of pure GeO(2) and SiO(2)-substituted GeO(2) materials with the α-quartz structure. These piezoelectric materials were obtained in millimeter size as well-faceted, visually colorless, and transparent crystals. Cubic-like or hexagonal prism-like morphology was identified depending on the chemical composition of the single-crystals and on the nature of the flux. Both the silicon substitution rate and the homogeneity of its distribution were estimated by Energy Dispersive X-ray spectroscopy. The cell parameters of the flux-grown GeO(2) and Ge(1-x)Si(x)O(2) (0.038 ≤ x ≤ 0.089) solid-solution were deduced from their X-ray powder diffraction pattern. As expected, the cell volumes decrease as the silicon content substitution increases. A room temperature Infrared spectroscopy study confirms the absence of hydroxyl groups in the as-grown crystals. Unlike what was observed for hydrothermally grown GeO(2) crystals, these flux-grown oxide materials did not present any phase transition before melting as pointed out by a Differential Scanning Calorimetry study. Neither a α-quartz/β-quartz transition as encountered in SiO(2) near 573 °C nor a α-quartz to rutile transformation were detected for these GeO(2) and Ge(1-x)Si(x)O(2) single-crystals.