OBJECTIVE: To evaluate the influence of different surface treatments on the microtensile bond strength of resin cement to zirconia ceramic. MATERIALS AND METHODS: Twelve cylinder-shaped (∅ 12×5.25 mm high) blocks of a commercial zirconium-oxide ceramic (Cercon® Zirconia, DENTSPLY) were randomly divided into 4 groups (n=3), based on the surface treatment to be performed: (1) airborne particle abrasion with 125 μm Al₂O₃ particles (S); (2) selective infiltration etching (SIE); (3) experimental hot etching solution applied for 30 min (ST) and (4) no treatment (C). Paradigm MZ100 blocks (3M ESPE) were cut into twelve cylinders of 4mm in thickness. Composite cylinders were bonded to conditioned ceramics using a resin cement (Calibra®, DENTSPLY), in combination with the proprietary adhesive system. After 24h bonded specimens were cut into microtensile sticks and loaded in tension until failure. Bond strength data were analyzed with Kruskall-Wallis and Dunn's Multiple Range test for multiple comparisons (p < 0.05). Failure mode distribution was recorded and the interfacial morphology of debonded specimens was analyzed using a scanning electron microscope (SEM). RESULTS: Bond strength values achieved after SIE and ST treatment were significantly higher than after S treatment and without any treatment (p < 0.05). Premature failures were mostly recorded in the S group. SIGNIFICANCE: Conditioning the high-strength ceramic surface with SIE and ST treatments yielded higher bond strengths of the resin cement than when zirconia ceramic was treated with airborne particle abrasion or left untreated.
OBJECTIVE: To evaluate the influence of different surface treatments on the microtensile bond strength of resin cement to zirconia ceramic. MATERIALS AND METHODS: Twelve cylinder-shaped (∅ 12×5.25 mm high) blocks of a commercial zirconium-oxide ceramic (Cercon® Zirconia, DENTSPLY) were randomly divided into 4 groups (n=3), based on the surface treatment to be performed: (1) airborne particle abrasion with 125 μm Al₂O₃ particles (S); (2) selective infiltration etching (SIE); (3) experimental hot etching solution applied for 30 min (ST) and (4) no treatment (C). Paradigm MZ100 blocks (3M ESPE) were cut into twelve cylinders of 4mm in thickness. Composite cylinders were bonded to conditioned ceramics using a resin cement (Calibra®, DENTSPLY), in combination with the proprietary adhesive system. After 24h bonded specimens were cut into microtensile sticks and loaded in tension until failure. Bond strength data were analyzed with Kruskall-Wallis and Dunn's Multiple Range test for multiple comparisons (p < 0.05). Failure mode distribution was recorded and the interfacial morphology of debonded specimens was analyzed using a scanning electron microscope (SEM). RESULTS: Bond strength values achieved after SIE and ST treatment were significantly higher than after S treatment and without any treatment (p < 0.05). Premature failures were mostly recorded in the S group. SIGNIFICANCE: Conditioning the high-strength ceramic surface with SIE and ST treatments yielded higher bond strengths of the resin cement than when zirconia ceramic was treated with airborne particle abrasion or left untreated.
Authors: Abbas Azari; Sakineh Nikzad; Arash Yazdani; Faezeh Atri; Abbas Fazel Anvari-Yazdi Journal: J Mater Sci Mater Med Date: 2017-06-14 Impact factor: 3.896