Bond strength of newer dentin bonding agents in different clinical situations.

This study compared the tensile bond strengths of different adhesive systems to different dentinal substrate conditions. The adhesive systems used were Adper Single Bond 2 total etch, XP Bond total etch, and two all-in-one adhesives, Adper Easy One and Xeno V. Ninety-six intact human premolars extracted on periodontal or orthodontic grounds were collected and stored in 0.9% physiologic saline for less than four weeks. Teeth were carefully cleaned to remove the soft tissue remnants. The occlusal surfaces were ground until the level of the dentinoenamel junction, exposing superficial dentin using a low-speed diamond disc. A standard smear layer was produced by wet sanding the dentin surface with 600-grit silicon carbide sandpaper for 40 seconds. The 96 specimens were embedded in autopolymerizing acrylic resin and divided into four groups of 24 each based on the dentin bonding agents used. Each group consisted of 24 specimens, which were further divided into two subgroups of 12 specimens each, moist dentin and dentin air-dried for 10 seconds. The regions of interest for adhesion were demarcated in each sample using adhesive tape, with a 4-mm–diameter hole isolating the peripheral region, and each adhesive system was employed. Four adhesive systems, two total etch and two self-etching adhesive, were applied to different dentinal substrates as per the manufacturers' instructions. Following the adhesive application, the specimens were restored with composite material using a metallic mold measuring 5 mm in diameter and 5 mm in height to keep the material in cylindrical form and were light cured per manufacturers' instructions. After being stored for 24 hours in distilled water at room temperature, the specimens were thermocycled for 550 cycles at temperatures ranging from 5°C to 60°C with a dwell time of 15 seconds in each bath and a transfer time of five seconds. The tensile bond strengths were determined using a Universal loading machine (Lloyd Universal Testing Machine) at a cross-head speed of 1 mm/min. On moist dentin, total-etch adhesives showed higher bond strength than did the all-in-one adhesives. Under the dry dentin condition, XP Bond exhibited significantly higher bond strength than did the Adper Single Bond 2 and two all-in-one adhesives, Adper Easy One and Xeno V.