Enhanced electrochemiluminescence from luminol at multi-walled carbon nanotubes decorated with palladium nanoparticles: a novel route for the fabrication of an oxygen sensor and a glucose biosensor.

Incorporation of palladium nanoparticles on the surface of multi-walled carbon nanotubes and modification of glassy carbon electrode with the prepared nano-hybrid material led to the fabrication of a novel electrode. The modified electrode showed attractive electrocatalytic activity and sensitizing effect on luminol-O(2) and luminol-H(2)O(2) electrochemiluminescence (ECL) reactions at neutral media. The sensitized luminol-O(2) and luminol-H(2)O(2) reactions were successfully applied for the ECL determination of dissolved O(2) and glucose, respectively. Under the optimal conditions for luminol-O(2) system, the ECL signal intensity of luminol was linear with the concentration of dissolved oxygen in the range between 0.08 and 0.94 mM (r=0.9996) and for luminol-H(2)O(2) system, the ECL signal intensity of luminol was linear with the concentration of glucose in the range between 0.1 and 1000 μM (r=0.9998). The limits of detection (S/N=3) for dissolved oxygen and glucose were 0.02 mM and 54 nM, respectively. The relative standard deviations (RSD) for repetitive measurements of 0.50 mM oxygen (n=10) and 10 μM glucose (n=30) were 3.5% and 0.3%, respectively. Also, under the optimal conditions for luminol-H(2)O(2) system, the ECL signal intensity of luminol was linear with the concentration of H(2)O(2) in the range between 1 nM and 0.45 mM (r=0.9997). The limit of detection (S/N=3) for H(2)O(2) detection was 0.5 nM and the relative standard deviation for repetitive measurements of 10 μM H(2)O(2) (n=10) was 0.8%.