PURPOSE: To investigate the muco/bioadhesive properties of chitosan, polyvinylpyrrolidone (PVP), and chitosan/PVP blends and the release of amoxicillin (AMX) contained in AMX-alginate beads coated with these materials. METHOD: Chitosan, PVP, and chitosan/PVP blends at various volume ratios were coated onto calcium alginate beads containing AMX. The muco/bioadhesive properties of all materials and the AMX-alginate beads coated with these materials were characterized. RESULTS: Measurements of their viscosity, texture, and adhesion to HT29 cells demonstrated that chitosan/PVP at a volume ratio of 5/5 had the best muco/bioadhesive properties when compared with chitosan, PVP, and blends of other ratios. Wash-off tests indicated that the mucoadhesive property of the coated AMX-alginate beads was significantly higher than that of the uncoated beads. Diffuse reflectance infrared Fourier transform spectroscopy showed that there were interactions between chitosan-PVP, chitosan-mucin, PVP-mucin, and chitosan/PVP blend-mucin. Scanning electron microscopy revealed that the surfaces of the coated beads were smoother than those of the uncoated beads. All coated AMX-alginate beads were able to provide a controlled release of AMX with Super Case II transport properties, at a pH of 4. This was probably a result of the rapid and extensive swelling of the alginate beads. The more rapid release of AMX at pH 1 was probably because of the rapid dissolution of the drug at this pH. CONCLUSIONS: From the controlled drug release and muco/bioadhesive properties of these coated AMX-alginate beads, we suggest that the alginate-coated beads might be a promising drug delivery system to assist with the eradication of Helicobacter pylori infections.
PURPOSE: To investigate the muco/bioadhesive properties of chitosan, polyvinylpyrrolidone (PVP), and chitosan/PVP blends and the release of amoxicillin (AMX) contained in AMX-alginate beads coated with these materials. METHOD: Chitosan, PVP, and chitosan/PVP blends at various volume ratios were coated onto calcium alginate beads containing AMX. The muco/bioadhesive properties of all materials and the AMX-alginate beads coated with these materials were characterized. RESULTS: Measurements of their viscosity, texture, and adhesion to HT29 cells demonstrated that chitosan/PVP at a volume ratio of 5/5 had the best muco/bioadhesive properties when compared with chitosan, PVP, and blends of other ratios. Wash-off tests indicated that the mucoadhesive property of the coated AMX-alginate beads was significantly higher than that of the uncoated beads. Diffuse reflectance infrared Fourier transform spectroscopy showed that there were interactions between chitosan-PVP, chitosan-mucin, PVP-mucin, and chitosan/PVP blend-mucin. Scanning electron microscopy revealed that the surfaces of the coated beads were smoother than those of the uncoated beads. All coated AMX-alginate beads were able to provide a controlled release of AMX with Super Case II transport properties, at a pH of 4. This was probably a result of the rapid and extensive swelling of the alginate beads. The more rapid release of AMX at pH 1 was probably because of the rapid dissolution of the drug at this pH. CONCLUSIONS: From the controlled drug release and muco/bioadhesive properties of these coated AMX-alginate beads, we suggest that the alginate-coated beads might be a promising drug delivery system to assist with the eradication of Helicobacter pylori infections.