Impact ionisation spectra from hypervelocity impacts using aliphatic poly(methyl methacrylate) microparticle projectiles.

We report impact ionisation spectra from spherical poly(methyl methacrylate) (PMMA) microparticles of 724 nm diameter impacting a rhodium target. These projectiles were coated with an ultrathin (~11 nm) overlayer of polypyrrole, an electrically conducting organic polymer; this enabled the accumulation of sufficient surface charge to allow electrostatic acceleration up to speeds of 4 to 8 km s(-1) using a high-voltage Van de Graaff instrument. A grid above the target (held at 3.33 kV cm(-1) with respect to the target) accelerated the cations that were generated during the hypervelocity impacts, and these ions then drifted to a charge detector. By measuring the collected charge vs. time and assuming only single ionisation events, time-of-flight mass spectra were obtained. Strong signals were observed for cationic species with ions of m/z 41, 65 and 115. There were also minor contributions from cations with masses ranging from m/z 29 to 142. The three major signals are assigned to fragment ions (C(3)H(5)(+), C(4)H(5)O(+)/C(5)H(9)(+) and C(6)H(11)O(2)(+)) which are known to be associated with the decomposition of PMMA. These impact ionisation spectra differ significantly from those reported earlier using polystyrene (PS) microparticles. The aliphatic PMMA microparticles generate small (m/z <100) fragment ions more readily at lower speeds than the predominantly aromatic PS microparticles, where speeds of at least 10 km s(-1) are typically required for substantial yields of low-mass fragment ions. This correlates well with the well-known greater chemical and thermal fragility of PMMA compared to PS. The PMMA microparticles should prove useful synthetic mimics for aliphatic carbonaceous micrometeorites.