AIM: To compare the subcutaneous tissue response to grey mineral trioxide aggregate (GMTA), white mineral trioxide aggregate (WMTA) and a new experimental cement (calcium enriched cement, CEM). METHODOLOGY: Thirty-six Wistar male albino rats each received three implants, containing one of the tested materials, and an empty tube as a control. Seven, 30 and 60 days after implantation, the animals were sacrificed. After histological preparation and H&E staining, the specimens were evaluated for capsule thickness, necrosis, and for the type, the severity, and the extent of inflammation. Kruskal Wallis and Chi-square tests were used for data analysis. RESULTS: After 1 week, CEM produced no necrosis compared to both types of WMTA and GMTA (P = 0.007). After 30 days, GMTA specimens had significantly less inflammation compared with WMTA and CEM (P = 0.011). After 60 days, less inflammation was associated with CEM specimens (P = 0.0001) compared to the other materials. Dystrophic calcifications in the connective tissue adjacent to all experimental material were detected. CONCLUSION: Histological observation illustrated that all materials were well tolerated by the subcutaneous tissues.
AIM: To compare the subcutaneous tissue response to grey mineral trioxide aggregate (GMTA), white mineral trioxide aggregate (WMTA) and a new experimental cement (calcium enriched cement, CEM). METHODOLOGY: Thirty-six Wistar male albino rats each received three implants, containing one of the tested materials, and an empty tube as a control. Seven, 30 and 60 days after implantation, the animals were sacrificed. After histological preparation and H&E staining, the specimens were evaluated for capsule thickness, necrosis, and for the type, the severity, and the extent of inflammation. Kruskal Wallis and Chi-square tests were used for data analysis. RESULTS: After 1 week, CEM produced no necrosis compared to both types of WMTA and GMTA (P = 0.007). After 30 days, GMTA specimens had significantly less inflammation compared with WMTA and CEM (P = 0.011). After 60 days, less inflammation was associated with CEM specimens (P = 0.0001) compared to the other materials. Dystrophic calcifications in the connective tissue adjacent to all experimental material were detected. CONCLUSION: Histological observation illustrated that all materials were well tolerated by the subcutaneous tissues.