H(2)O(2)-sensitized TiO(2)/SiO(2) composites with high photocatalytic activity under visible irradiation.

TiO(2)/SiO(2) composite photocatalysts were prepared by depositing of TiO(2) onto nano-SiO(2) particles. X-ray diffraction (XRD), transmission electron micrograph (TEM), Raman spectrometer, UV-Vis diffuse reflectance spectroscopy, Fourier transform infrared spectroscopy (FT-IR) were employed to characterize the properties of the synthesized TiO(2)/SiO(2) composites. These results indicated that the products without calcination were amorphous, and calcination could enhance the crystallinity of TiO(2). Increases in the amount of TiO(2) would decrease the dispersion in the composites. H(2)O(2)-sensitized TiO(2)/SiO(2) composite photocatalysts could absorb visible light at wavelength below 550 nm. The photocatalytic activity of as-prepared catalysts was characterized by methyl-orange degradation. The results showed the uncalcined composite photocatalysts with amorphous TiO(2) exhibited higher photocatalytic activity under visible light, and the activity of catalysts with TiO(2) content over 30% decreased with increasing of TiO(2) content. Increases in the calcination temperature and TiO(2) content promote the formation of bulk TiO(2) and result in a decrease in activity. Crown