Jylan El Guindy1, Manar Y Fouda. 1. Department of Fixed Prosthodontics, Faculty of Oral and Dental Medicine, Cairo University, Giza, Cairo, Egypt. dr_jul@hotmail.com
Abstract
PURPOSE: The aim of this study was to assess the role of obturating systems, dowel materials, and adhesive techniques on the resistance to fracture of endodontically treated teeth. MATERIAL AND METHODS: Eighty maxillary central incisors were selected and randomly divided into two groups according to the obturating system (n = 40); group I: gutta-percha and Roeko sealer; group II: RealSeal. Both groups were further subdivided into two subgroups; subgroup A: using ceramic dowels (Cosmopost); subgroup B using fiber dowels (Easy Post). Each subgroup was assigned to two divisions according to the adhesive luting technique; division V (total-etch) Variolink II resin cement; division U (self-adhesive) RelyX Unicem. Composite core build-up was made using a core former. Each specimen was loaded 2 mm from its incisal edge on the palatal side at a 135° angle with the long axis of the tooth using a universal testing machine with a load cell of 5 KN at a crosshead speed of 0.5 mm/min until fracture. Failure loads were recorded in N. Scanning electron microscopic examination at the dentin/resin interface (1000x) was performed. Three-way ANOVA was used to test the effect of obturating system, dowel material, adhesive technique, and their interactions (obturating system * dowel material, obturating system * adhesive, dowel material * adhesive, obturating system * dowel material * adhesive). Duncan's test was used for pairwise comparison. The significance level was set at p≤ 0.05. Statistical analysis was performed with SPSS 16.0. RESULTS: The mean resistance to fracture (617.4 N) was statistically significantly higher in the ceramic dowel with gutta-percha and Variolink (GP/C/V) group than in the other groups. The RealSeal and RelyX fiber dowel group's mean resistance was the lowest and was significantly lower than the other groups. CONCLUSIONS: In this study, three factors played a part in enhancing the resistance to fracture of endodontically treated teeth. High resistance to fracture was achieved when ceramic dowels were luted with total-etch technique in gutta-percha-obturated teeth.
PURPOSE: The aim of this study was to assess the role of obturating systems, dowel materials, and adhesive techniques on the resistance to fracture of endodontically treated teeth. MATERIAL AND METHODS: Eighty maxillary central incisors were selected and randomly divided into two groups according to the obturating system (n = 40); group I: gutta-percha and Roeko sealer; group II: RealSeal. Both groups were further subdivided into two subgroups; subgroup A: using ceramic dowels (Cosmopost); subgroup B using fiber dowels (Easy Post). Each subgroup was assigned to two divisions according to the adhesive luting technique; division V (total-etch) Variolink II resin cement; division U (self-adhesive) RelyX Unicem. Composite core build-up was made using a core former. Each specimen was loaded 2 mm from its incisal edge on the palatal side at a 135° angle with the long axis of the tooth using a universal testing machine with a load cell of 5 KN at a crosshead speed of 0.5 mm/min until fracture. Failure loads were recorded in N. Scanning electron microscopic examination at the dentin/resin interface (1000x) was performed. Three-way ANOVA was used to test the effect of obturating system, dowel material, adhesive technique, and their interactions (obturating system * dowel material, obturating system * adhesive, dowel material * adhesive, obturating system * dowel material * adhesive). Duncan's test was used for pairwise comparison. The significance level was set at p≤ 0.05. Statistical analysis was performed with SPSS 16.0. RESULTS: The mean resistance to fracture (617.4 N) was statistically significantly higher in the ceramic dowel with gutta-percha and Variolink (GP/C/V) group than in the other groups. The RealSeal and RelyX fiber dowel group's mean resistance was the lowest and was significantly lower than the other groups. CONCLUSIONS: In this study, three factors played a part in enhancing the resistance to fracture of endodontically treated teeth. High resistance to fracture was achieved when ceramic dowels were luted with total-etch technique in gutta-percha-obturated teeth.