Effect of doping on the morphology and multiferroic properties of BiFeO3 nanorods.

In this study we report the synthesis of BiFeO(3) nanorods using a sonochemical technique. The nanorods had a diameter of 20-50 nm, a length of 100-500 nm and exhibit aspect ratios in the range of 5-10. However, after doping, the TEM images of Bi(0.9)Ba(0.1)Fe(0.9)Mn(0.1)O(3) and Bi(0.9)Ca(0.1)Fe(0.9)Cr(0.1)O(3) samples show that the aspect ratios of both the double doped samples have reduced considerably, while retaining the crystallinity of the particles. BiFeO(3) nanorods show a weak ferromagnetic order at room temperature, which is quite different from the linear M-H relationship reported for bulk BiFeO(3). The saturation magnetization of these BiFeO(3) nanostructures has been found to increase on doping with various metal ions (Ba(2+), Ca(2+), Mn(2+), Cr(3+)), reaching a maximum value of 1.35 emu g(-1) for the Bi(0.9)Ba(0.1)Fe(0.9)Mn(0.1)O(3) nanostructures. However, saturation of electric polarization was observed only in case of the Bi(0.9)Ca(0.1)Fe(0.9)Cr(0.1)O(3) nanostructures.