Synthesis of thick mesoporous gamma-alumina films, loading of Pt nanoparticles, and use of the composite film as a reusable catalyst.

Nanocrystalline mesoporous gamma-Al2O3 film of high thickness has been developed and characterized. The films were prepared on ordinary glass substrates by a single dip-coating method using boehmite (AlOOH) sols derived from aluminum tri-sec-butoxide in presence of cetyltrimethylammonium bromide (CTAB) as structure-directing agent. The dried films were heat-treated at 500 degrees C in air to remove the organics and strengthen the network. The GIXRD of the heat-treated (500 degrees C) film shows a broad peak in the low-angle region supporting the formation of worm-hole-like disordered mesostructures. The high-angle GIXRD, FTIR, and TEM of the films confirm the formation of gamma-Al2O3. N2 adsorption-desorption analyses showed that the heat-treated (500 degrees C) film has a BET surface area of 171 m(2) g(-1) with a pore volume of 0.188 cm(3) g(-1) and mean pore diameter 4.3 nm. Pt nanoparticles (NPs) (approximately 2.7 mol % with respect to the equivalent AlO(1.5)) were generated inside the mesopores of the heat-treated films simply by soaking H2PtCl6 solutions into it, and followed by thermal decomposition at 500 degrees C. The surface area and pore volume of the Pt-incorporated film have been reduced to 101 m(2) g(-1) and 0.119 cm(3) g(-1) respectively, confirming the inclusion of Pt NPs inside the pores. FESEM and TEM studies revealed uniform distribution of Pt NPs (2-8.5 nm; average diameter 4.9 nm) in the films. Catalytic properties of the Pt-incorporated films were investigated in two model (one inorganic and other organic) systems: reduction of hexacyanoferrate(III) ions by thiosulfate to ferrocyanide, and p-nitrophenol to p-aminophenol. In both the cases, the catalyst showed excellent activities, and the reduction reactions followed smoothly, showing isosbestic points in the UV-visible spectra. The catalyst films can be separated easily after the reactions and reused several times.