Structural characterisation of the Li argyrodites Li7PS6 and Li7PSe6 and their solid solutions: quantification of site preferences by MAS-NMR spectroscopy.

Li(7)PS(6) and Li(7)PSe(6) belong to a class of new solids that exhibit high Li(+) mobility. A series of quaternary solid solutions Li(7)PS(6-x)Se(x) (0 < or = x < or = 6) were characterised by X-ray crystallography and magic-angle spinning nuclear magnetic resonance (MAS-NMR) spectroscopy. The high-temperature (HT) modifications were studied by single-crystal investigations (both F43m, Z=4, Li(7)PS(6): a=9.993(1) A, Li(7)PSe(6): a=10.475(1) A) and show the typical argyrodite structures with strongly disordered Li atoms. HT-Li(7)PS(6) and HT-Li(7)PSe(6) transform reversibly into low-temperature (LT) modifications with ordered Li atoms. X-ray powder diagrams show the structures of LT-Li(7)PS(6) and LT-Li(7)PSe(6) to be closely related to orthorhombic LT-alpha-Cu(7)PSe(6). Single crystals of the LT modifications are not available due to multiple twinning and formation of antiphase domains. The gradual substitution of S by Se shows characteristic site preferences closely connected to the functionalities of the different types of chalcogen atoms (S, Se). High-resolution solid-state (31)P NMR is a powerful method to differentiate quantitatively between the distinct (PS(4-n)Se(n))(3-) local environments. Their population distribution differs significantly from a statistical scenario, revealing a pronounced preference for P-S over P-Se bonding. This preference, shown for the series of LT samples, can be quantified in terms of an equilibrium constant specifying the melt reaction Se(P)+S(2-) <==>S(P)+Se(2-), prior to crystallisation. The (77)Se MAS-NMR spectra reveal that the chalcogen distributions in the second and third coordination sphere of the P atoms are essentially statistical. The number of crystallographically independent Li atoms in both LT modifications was analysed by means of (6)Li{(7)Li} cross polarisation magic angle spinning (CPMAS).