Room temperature ferromagnetism in Fe-doped CeO2 nanoparticles.

RT ferromagnetism was observed in nanoparticles of Fe-doped CeO2 (i.e., Ce(0.97)Fe(0.03)O2) synthesized by a sol-gel method. The undoped and Fe-doped CeO2 were characterized by XRD, Raman spectroscopy, TEM, and VSM. The undoped samples and Ce(0.97)Fe(0.03)O2 precursor exhibit a diamagnetic behavior. The 673 K-calcined Ce(0.97)Fe(0.03)O2 sample is paramagnetic whereas 773 and 873 K-calcined Ce(0.97)Fe(0.03)O2 samples are ferromagnetism having the magnetizations of 4.65 x 10(-3) emu/g and 6.20 x 10(-3) emu/g at 10 kOe, respectively. Our results indicate that the ferromagnetic property is intrinsic to the Fe-doped CeO2 system and is not a result of any secondary magnetic phase or cluster formation.