Canola straw as a bio-waste resource for medium density fiberboard (MDF) manufacture.

Canola straw as an agricultural residue has been investigated for MDF production. The variables were steaming time (2, 5 and 8 min), the resin content (9% and 11%), and press time (4 and 6 min). Common physical and mechanical properties of experimental boards including modulus of rupture (MOR), modulus of elasticity (MOE), internal bond strength (IB) and thickness swelling (TS) were measured. Fiber properties of canola straw including length, diameter and cell wall thickness were determined. The results showed that all the tested mechanical properties improved with the increase of steaming time level. The results were close to the minimum requirements of MDF specified in the ANSI A208.2 standard. Dimensional stability of the MDFs improved as adhesive content increased. The IB values are positively affected by the increase of press time. MDF properties made from canola straw possess acceptable qualities as compared to those made from other non-wood plants. Furthermore, the fiber dimensions of canola straw were also in the range of reported values in hardwoods.