PURPOSE: To assess the effect of a horizontally transfixed fiber glass post placed between buccal and palatal surfaces, on the fracture strength of endodontically treated molar teeth with MOD cavities, either restored with resin-based composite, or not. METHODS:75 sound maxillary human third molars were extracted, embedded in acrylic resin blocks and randomly assigned to five groups (n=15). Group A (sound teeth), (control) and Groups B, C, D and E, which were subjected to the following procedures after endodontic treatment: GB--(MOD+Endo), GC--(MOD+Endo+Post), GD--MOD and composite restoration (MOD+Endo+CR), GE--(MOD+Endo+Post+CR). The specimens were stored in distilled water at 37 degrees C for 24 hours. Later, a compressive force was applied by means of a universal testing machine at 1 mm/minute speed, parallel to the long axis of the teeth until fracture occurred. RESULTS: The means of the results (N) followed by the same letter represent no statistical difference by ANOVA and Tukey (P<0.05): GA = 4289.8 (+/- 1128.9)a, GB = 549.6 (+/- 120.7)b, GC = 1474.8 (+/- 338.1)c, GD = 1224.7 (+/- 236.0)c, GE = 2645.4 (+/- 675.1)d. In the analysis of qualitative variables, there was a tendency to cusp fracture in all groups except for Group C. The fiber glass post transfixed horizontally in a MOD cavity significantly increased the fracture resistance of the teeth restored with resin composite.
RCT Entities:
PURPOSE: To assess the effect of a horizontally transfixed fiber glass post placed between buccal and palatal surfaces, on the fracture strength of endodontically treated molar teeth with MOD cavities, either restored with resin-based composite, or not. METHODS: 75 sound maxillary human third molars were extracted, embedded in acrylic resin blocks and randomly assigned to five groups (n=15). Group A (sound teeth), (control) and Groups B, C, D and E, which were subjected to the following procedures after endodontic treatment: GB--(MOD+Endo), GC--(MOD+Endo+Post), GD--MOD and composite restoration (MOD+Endo+CR), GE--(MOD+Endo+Post+CR). The specimens were stored in distilled water at 37 degrees C for 24 hours. Later, a compressive force was applied by means of a universal testing machine at 1 mm/minute speed, parallel to the long axis of the teeth until fracture occurred. RESULTS: The means of the results (N) followed by the same letter represent no statistical difference by ANOVA and Tukey (P<0.05): GA = 4289.8 (+/- 1128.9)a, GB = 549.6 (+/- 120.7)b, GC = 1474.8 (+/- 338.1)c, GD = 1224.7 (+/- 236.0)c, GE = 2645.4 (+/- 675.1)d. In the analysis of qualitative variables, there was a tendency to cusp fracture in all groups except for Group C. The fiber glass post transfixed horizontally in a MOD cavity significantly increased the fracture resistance of the teeth restored with resin composite.