N Hiraishi1, C K Y Yiu, N M King, F R Tay. 1. Paediatric Dentistry and Orthodontics, The University of Hong Kong, Prince Philip Dental Hospital, 34 Hospital Road, Pokfulam, Hong Kong SAR, China. hiraishinoriko@yahoo.com
Abstract
OBJECTIVES: The aim of this study was to investigate the effect of pre-treatment by chlorhexidine on the microtensile bond strength (mTBS) of resin cements and nanoleakage at the resin-dentine interfaces. METHODS: Cylindrical composite blocks were luted to human dentine using resin cements (RelyX ARC, 3M ESPE: ARC; Panavia F, Kuraray Medical Inc.: PF; RelyX Unicem, 3M ESPE: UN) with/without pre-treatment by 2% chlorhexidine digluconate (CAVITY CLEANSER, Bisco, Inc., Schaumburg, IL, USA). CAVITY CLEANSER was applied on the acid etched dentine for 60s in the ARC group, and on smear layer-covered dentine in the PF and UN groups. After storage in water for 24h, the bonded teeth were sectioned into 1mm thick slabs and further into 0.9mm x 0.9mm beams. After immersion in water or ammoniacal silver nitrate for 24h, the beams were stressed to failure in tension. The fractured surfaces were examined by field-emission scanning electron microscopy (FE-SEM) using backscattered electron mode. The silver-stained slabs were used to examine nanoleakage within the bonded interface by FE-SEM. RESULTS: The resin cement and chlorhexidine treatment had significant effects (p<0.0001) on mTBS; while the storage media had no significant effect (p=0.435). The mTBS of ARC was significantly higher than the other cements. Chlorhexidine reduced mTBS and produced pronounced nanoleakage when PF and UC were luted to dentine. CONCLUSIONS: Pre-treatment with chlorhexidine affected the integrity of dentine bonding with PF and UC, while there was no adverse effect on coupling of ARC.
RCT Entities:
OBJECTIVES: The aim of this study was to investigate the effect of pre-treatment by chlorhexidine on the microtensile bond strength (mTBS) of resin cements and nanoleakage at the resin-dentine interfaces. METHODS: Cylindrical composite blocks were luted to human dentine using resin cements (RelyX ARC, 3M ESPE: ARC; Panavia F, Kuraray Medical Inc.: PF; RelyX Unicem, 3M ESPE: UN) with/without pre-treatment by 2% chlorhexidine digluconate (CAVITY CLEANSER, Bisco, Inc., Schaumburg, IL, USA). CAVITY CLEANSER was applied on the acid etched dentine for 60s in the ARC group, and on smear layer-covered dentine in the PF and UN groups. After storage in water for 24h, the bonded teeth were sectioned into 1mm thick slabs and further into 0.9mm x 0.9mm beams. After immersion in water or ammoniacal silver nitrate for 24h, the beams were stressed to failure in tension. The fractured surfaces were examined by field-emission scanning electron microscopy (FE-SEM) using backscattered electron mode. The silver-stained slabs were used to examine nanoleakage within the bonded interface by FE-SEM. RESULTS: The resin cement and chlorhexidine treatment had significant effects (p<0.0001) on mTBS; while the storage media had no significant effect (p=0.435). The mTBS of ARC was significantly higher than the other cements. Chlorhexidine reduced mTBS and produced pronounced nanoleakage when PF and UC were luted to dentine. CONCLUSIONS: Pre-treatment with chlorhexidine affected the integrity of dentine bonding with PF and UC, while there was no adverse effect on coupling of ARC.
Authors: Ana Coelho; Inês Amaro; Ana Apolónio; Anabela Paula; José Saraiva; Manuel Marques Ferreira; Carlos Miguel Marto; Eunice Carrilho Journal: Int J Mol Sci Date: 2021-04-22 Impact factor: 5.923
Authors: Louis Hardan; Rim Bourgi; Carlos Enrique Cuevas-Suárez; Maciej Zarow; Naji Kharouf; Davide Mancino; Carlos Fernández Villares; Dariusz Skaba; Monika Lukomska-Szymanska Journal: Microorganisms Date: 2021-06-06