Bonding of adhesive resin luting agents to metal and amalgam.

The shear bond strength of three adhesives, Panavia 21, Superbond, All Bond C&B Cement, and a dual cure resin (Variolink), to Ni-Cr-Be (Rexillium III), Midigold (Type III gold) and Amalgam (Sybraloy) were determined. Fifteen samples were prepared using 800 grit abrasive papers for Ni-Cr and Midi-Gold, and 100 grit papers for amalgam. Ni-Cr-Be and Midi-Gold samples were sandblasted for 30 s and steam cleaned for 10 s. The adhesives were bonded to the samples using gelatine capsules and were matured for 24 h in water at 37 degrees C. The samples were debonded in shear using an Instron at a cross-head speed of 1 mm/min. The data was analysed using ANOVA and a Tukey test. The bond strength of Superbond to both metal alloys was significantly higher (P<0.05) than any of the materials tested, with the exception Panavia 21 to gold. The bond strength of All Bond C&B cement had shown to be not significant difference from those of Panavia 21 and Variolink, when bonded to Rexillium and Midi-Gold, respectively. The bond strength of All Bond C&B Cement to amalgam was significantly greater (P<0.05) than those of the other materials tested. The shear bond strength to gold showed lower bonding for all adhesives when compared with Rexillium (P<.001). The ranking of bond strength to both alloys was as follows: Superbond>Panavia 21>All Bond C&B>Variolink. The nature of substrate to be used for bonding and the adhesive material itself are important factors in bonding which can be achieved between cast metals and prepared teeth with amalgam filling. Superbond should be successful as an adhesive for the attachment of all substrates tested, with the possible exception of amalgam, for which All Bond C&B Cement gives the best result.