Amr S Fawzy1, Farid S El-Askary. 1. Department of Biomaterials, Faculty of Dentistry, Ain Shams University, Cairo, Egypt. amrshf@hotmail.com
Abstract
OBJECTIVE: The purpose of this study was to characterize the effects of either acidic or combined alkaline/heat treatments on the surface of grit-blasted commercially pure (cp) titanium. The effects of the previous treatments on the shear bond strength (SBS) of cp titanium to conventional glass ionomer, resin-reinforced glass ionomer and self-adhesive resin luting cements were evaluated. METHODS: Titanium discs were machined and received one of the following treatments; grit-blasting (GB), grit-blasting followed either by etching in HNO(3)/HF solution (GB/Ac) or by combined 5M NaOH treatment/heat treatment at 600 degrees C for 1h, then immersed for 24h in SBF solution before cementation (GB/Ak). The treated surfaces were characterized by atomic force microscope (AFM), scanning electron microscope (SEM) and laser-induced brake-down spectroscopy (LIBS). Discs were cemented either by Fuji I, Fuji Plus or Rely X Unicem luting cements. The SBS was evaluated and the debonded discs were investigated by SEM. RESULTS: Two prominent results were revealed; first, GB/Ak treatment showed the highest SBS than the other treatments (P<0.0001). Second, Rely X Unicem showed the highest SBS than the other cements (P<0.0001). Fuji I and Fuji Plus showed predominant cohesive type of failure, whereas Rely X showed predominant adhesive type of failure. SIGNIFICANCE: Combined alkaline/heat treatments of commercially pure titanium surface shows to be of beneficial effect in enhancing SBS to glass ionomer, resin-modified glass ionomer and adhesive resin luting cements.
OBJECTIVE: The purpose of this study was to characterize the effects of either acidic or combined alkaline/heat treatments on the surface of grit-blasted commercially pure (cp) titanium. The effects of the previous treatments on the shear bond strength (SBS) of cp titanium to conventional glass ionomer, resin-reinforced glass ionomer and self-adhesive resin luting cements were evaluated. METHODS:Titanium discs were machined and received one of the following treatments; grit-blasting (GB), grit-blasting followed either by etching in HNO(3)/HF solution (GB/Ac) or by combined 5M NaOH treatment/heat treatment at 600 degrees C for 1h, then immersed for 24h in SBF solution before cementation (GB/Ak). The treated surfaces were characterized by atomic force microscope (AFM), scanning electron microscope (SEM) and laser-induced brake-down spectroscopy (LIBS). Discs were cemented either by Fuji I, Fuji Plus or Rely X Unicem luting cements. The SBS was evaluated and the debonded discs were investigated by SEM. RESULTS: Two prominent results were revealed; first, GB/Ak treatment showed the highest SBS than the other treatments (P<0.0001). Second, Rely X Unicem showed the highest SBS than the other cements (P<0.0001). Fuji I and Fuji Plus showed predominant cohesive type of failure, whereas Rely X showed predominant adhesive type of failure. SIGNIFICANCE: Combined alkaline/heat treatments of commercially pure titanium surface shows to be of beneficial effect in enhancing SBS to glass ionomer, resin-modified glass ionomer and adhesive resin luting cements.