Sonochemical synthesis of monodispersed magnetite nanoparticles by using an ethanol-water mixed solvent.

The magnetite nanoparticles were synthesized in an ethanol-water solution under ultrasonic irradiation from a Fe(OH)(2) precipitate. XRD, TEM, TG, IR, VSM and UV/vis absorption spectrum were used to characterize the magnetite nanoparticles. It was found that the formation of magnetite was accelerated in ethanol-water solution in the presence of ultrasonic irradiation, whereas, it was limited in ethanol-water solution under mechanical stirring. The monodispersibility of magnetite particles was improved significantly through the sonochemical synthesis in ethanol-water solution. The magnetic properties were improved for the samples synthesized under ultrasonic irradiation. This would be attributed to high Fe(2+) concentration in the magnetite cubic structure.