Vesna Miletic1, Ario Santini, Ivan Trkulja. 1. Edinburgh Postgraduate Dental Institute, The University of Edinburgh, Lauriston Building (4th floor), Lauriston Place, Edinburgh EH3 9HA, United Kingdom. vesna.miletic@gmail.com
Abstract
OBJECTIVES: To quantify monomer elution from different adhesive systems using reverse-phase high-performance liquid chromatography (HPLC) and correlate this elution with the ratio of carbon-carbon double bonds from monomer to polymer (RDB) obtained using micro-Raman spectroscopy. METHODS: Thirty dentine discs were cut from 30 human, intact, third molars and randomly allocated to five groups according to the adhesive applied: total-etch, Excite (Ivoclar Vivadent), two-bottle self-etch, Clearfil SE (Kuraray), one-bottle self-etch, Clearfil 3S (Kuraray), ormocer-based, Admira (Voco) and Filtek Silorane adhesive system (FS) (3M ESPE). Monomer elution was studied 1h, 6h, 24h, 96h and 7 days after immersion in 75% ethanol/water. The RDB was calculated immediately after light-curing and thereafter at 24h and 7 days. The data were statistically analysed using one-way ANOVA and Pearson's correlation coefficient (p<0.05). RESULTS: More than 90% of the whole elution occurred during the first 1h, except for BisGMA in FS, with the highest absolute amount from Clearfil SE and the highest wt% from Admira. Initial RDB was in the ascending order FS<Admira<Excite<Clearfil SE<Clearfil 3S. In all groups, the RDB was significantly higher after 24h and 7 days than immediately after light-curing (p<0.05). Negative correlation was found only for the elution of HEMA and the RDB of Clearfil 3S. CONCLUSIONS: Different adhesive systems showed different monomer elution kinetics. In all systems, the RDB increased after monomer elution. Overall, no direct correlation exists between the RDB of adhesives and the elution of unreacted monomers.
OBJECTIVES: To quantify monomer elution from different adhesive systems using reverse-phase high-performance liquid chromatography (HPLC) and correlate this elution with the ratio of carbon-carbon double bonds from monomer to polymer (RDB) obtained using micro-Raman spectroscopy. METHODS: Thirty dentine discs were cut from 30 human, intact, third molars and randomly allocated to five groups according to the adhesive applied: total-etch, Excite (Ivoclar Vivadent), two-bottle self-etch, Clearfil SE (Kuraray), one-bottle self-etch, Clearfil 3S (Kuraray), ormocer-based, Admira (Voco) and Filtek Silorane adhesive system (FS) (3M ESPE). Monomer elution was studied 1h, 6h, 24h, 96h and 7 days after immersion in 75% ethanol/water. The RDB was calculated immediately after light-curing and thereafter at 24h and 7 days. The data were statistically analysed using one-way ANOVA and Pearson's correlation coefficient (p<0.05). RESULTS: More than 90% of the whole elution occurred during the first 1h, except for BisGMA in FS, with the highest absolute amount from Clearfil SE and the highest wt% from Admira. Initial RDB was in the ascending order FS<Admira<Excite<Clearfil SE<Clearfil 3S. In all groups, the RDB was significantly higher after 24h and 7 days than immediately after light-curing (p<0.05). Negative correlation was found only for the elution of HEMA and the RDB of Clearfil 3S. CONCLUSIONS: Different adhesive systems showed different monomer elution kinetics. In all systems, the RDB increased after monomer elution. Overall, no direct correlation exists between the RDB of adhesives and the elution of unreacted monomers.