Interaction of fullerene (C60) nanoparticles with humic acid and alginate coated silica surfaces: measurements, mechanisms, and environmental implications.

The deposition kinetics of fullerene (C60) nanoparticles onto bare silica surfaces and surfaces precoated with humic acid and alginate are investigated over a range of monovalent (NaCI) and divalent (CaCl2) salt concentrations using a quartz crystal microbalance. Because simultaneous aggregation of the fullerene nanoparticles occurs, especially at higher electrolyte concentrations, we normalize the observed deposition rates by the corresponding favorable (transport-limited) deposition rates to obtain the attachment efficiencies, alpha. The deposition kinetics of fullerene nanoparticles onto bare silica surfaces are shown to be controlled by electrostatic interactions and van der Waals attraction, consistent with the classical particle deposition behavior where both favorable and unfavorable deposition regimes are observed. The presence of dissolved humic acid and alginate in solution leads to significantly slower deposition kinetics due to steric repulsion. Precoating the silica surfaces with humic acid and alginate exerts similar steric stabilization in the presence of NaCl. In the presence of CaCl2, the deposition kinetics of fullerene nanoparticles onto both humic acid- and alginate-coated surfaces are relatively high, even at relatively low (0.3 mM) calcium concentration. This behavior is attributed to the macromolecules undergoing complex formation with calcium ions, which reduces the charge and steric influences of the adsorbed macromolecular layers.