Property changes of powdery polyacrylonitrile synthesized by aqueous suspension polymerization during heat-treatment process under air atmosphere.

High molecular weight powdery polyacrylonitrile (PAN) polymers were prepared by aqueous suspension polymerization employing itaconic acid (IA) as comonomer and alpha,alpha(')-azobisisobutyronitrile (AIBN) as initiator at 60 degrees C. PAN polymers obtained with different monomer ratios were characterized by EA, DSC, FTIR and XRD. It is investigated that the oxygen element content in PAN polymers increased with the increase of required IA amounts in the feed and heat-treatment temperatures. DSC curves of PAN copolymers exhibited the triplet character, owing to the exothermic cyclization and oxidative reactions during heat-treatment process. Introduction of IA in the feed relaxed exothermic reactions of PAN polymers under air atmosphere. Structure and crystallinity changes were affected by required IA amounts in the feed and enhancement of heat-treatment temperatures. The characteristic functional groups (including C[triple bond]N, C=O, CH(2)) presented in FTIR spectra of PAN polymers indicated copolymerization reaction of AN and IA. Existence of some organic groups (C-O, C=C and/or C=N) indicated formation of ladderlike structure during heat-treatment process. PAN homopolymer had the better crystallinity (mainly peak intensity and peak area around 2theta = 17 degrees) than most RT-PAN copolymers. When heat-treatment temperature is around 210 degrees C, peak intensity, peak area, L(c) and CI of HT-PAN polymers corresponding to samples 1# and 2# got maxima, while crystallinity became weak at higher heat-treatment temperatures.