High efficiency NbN nanowire superconducting single photon detectors fabricated on MgO substrates from a low temperature process.

We demonstrate high-performance nanowire superconducting single photon detectors (SSPDs) on bN thin films grown at a temperature compatible with monolithic integration. NbN films ranging from 150 nm to 3 nm in thickness were deposited by dc magnetron sputtering on MgO substrates at 400 degrees C SSPDs were fabricated on high quality NbN films of different thickness (7 to 3 nm) deposited under optimal conditions. Electrical and optical characterizations were performed on the SSPDs. The highest QE value measured at 4.2K is 20% at 1300 nm.