PURPOSE: To investigate the penetration (tags) of adhesive materials into enamel etched with phosphoric acid or treated with a self-etching adhesive, before application of a pit-and-fissure sealant. MATERIALS AND METHODS: The sample comprised six study groups with six specimens each. Before pit-and-fissure sealing with the materials Clinpro SealantTM (Groups I and II), Vitro Seal ALPHA (Groups III and IV) and Fuji II LC (Groups V and VI), the teeth in Groups I, III, and V were etched with 35% phosphoric acid for 30 seconds. Teeth in Groups II, IV, and VI received application of the self-etching adhesive Adper Prompt L-Pop. The treated teeth were sectioned buccolingually, ground to 100-microm thickness, decalcified, and analyzed by conventional light microscopy at 400x magnification. RESULTS: The teeth etched with phosphoric acid exhibited significantly greater penetration than specimens treated with self-etching adhesive. CLINICAL SIGNIFICANCE: When compared with enamel treated with a self-etching adhesive, the penetration (tags) of adhesive materials into enamel was greater when applied on enamel etched with phosphoric acid.
PURPOSE: To investigate the penetration (tags) of adhesive materials into enamel etched with phosphoric acid or treated with a self-etching adhesive, before application of a pit-and-fissure sealant. MATERIALS AND METHODS: The sample comprised six study groups with six specimens each. Before pit-and-fissure sealing with the materials Clinpro SealantTM (Groups I and II), Vitro Seal ALPHA (Groups III and IV) and Fuji II LC (Groups V and VI), the teeth in Groups I, III, and V were etched with 35% phosphoric acid for 30 seconds. Teeth in Groups II, IV, and VI received application of the self-etching adhesive Adper Prompt L-Pop. The treated teeth were sectioned buccolingually, ground to 100-microm thickness, decalcified, and analyzed by conventional light microscopy at 400x magnification. RESULTS: The teeth etched with phosphoric acid exhibited significantly greater penetration than specimens treated with self-etching adhesive. CLINICAL SIGNIFICANCE: When compared with enamel treated with a self-etching adhesive, the penetration (tags) of adhesive materials into enamel was greater when applied on enamel etched with phosphoric acid.