OBJECTIVES: The aim of the present study was to evaluate immunohistochemically the pattern of guided bone regeneration (GBR) using different types of barrier membranes. MATERIAL AND METHODS: Standardized buccal dehiscence defects were surgically created following implant bed preparation in 12 beagle dogs. Defects were randomly assigned to six different GBR procedures: a collagen-coated bone grafting material (BOC) in combination with either a native, three cross-linked, a titanium-reinforced collagen membrane, or expanded polytetrafluorethylene (ePTFE), or BOC alone. After 1, 2, 4, 6, 9, and 12 weeks of submerged healing, dissected blocks were processed for immunohistochemical (osteocalcin - OC, transglutaminase II - angiogenesis) and histomorphometrical analysis [e.g., bone-to-implant contact (BIC), area of new bone fill (BF)]. RESULTS: In general, angiogenesis, OC antigen reactivity, and new bone formation mainly arose from open bone marrow spaces at the bottom of the defect and invaded the dehiscence areas along the implant surface and BOC. At 4 weeks, membranes supporting an early transmembraneous angiogenesis also exhibited some localized peripheral areas of new bone formation. However, significantly increasing BIC and BF values over time were observed in all groups. Membrane exposure after 10-12 weeks was associated with a loss of the supporting alveolar bone in the ePTFE group. CONCLUSION: Within the limits of the present study, it was concluded that (i) angiogenesis plays a crucial role in GBR and (ii) all membranes investigated supported bone regeneration on an equivalent level.
OBJECTIVES: The aim of the present study was to evaluate immunohistochemically the pattern of guided bone regeneration (GBR) using different types of barrier membranes. MATERIAL AND METHODS: Standardized buccal dehiscence defects were surgically created following implant bed preparation in 12 beagle dogs. Defects were randomly assigned to six different GBR procedures: a collagen-coated bone grafting material (BOC) in combination with either a native, three cross-linked, a titanium-reinforced collagen membrane, or expanded polytetrafluorethylene (ePTFE), or BOC alone. After 1, 2, 4, 6, 9, and 12 weeks of submerged healing, dissected blocks were processed for immunohistochemical (osteocalcin - OC, transglutaminase II - angiogenesis) and histomorphometrical analysis [e.g., bone-to-implant contact (BIC), area of new bone fill (BF)]. RESULTS: In general, angiogenesis, OC antigen reactivity, and new bone formation mainly arose from open bone marrow spaces at the bottom of the defect and invaded the dehiscence areas along the implant surface and BOC. At 4 weeks, membranes supporting an early transmembraneous angiogenesis also exhibited some localized peripheral areas of new bone formation. However, significantly increasing BIC and BF values over time were observed in all groups. Membrane exposure after 10-12 weeks was associated with a loss of the supporting alveolar bone in the ePTFE group. CONCLUSION: Within the limits of the present study, it was concluded that (i) angiogenesis plays a crucial role in GBR and (ii) all membranes investigated supported bone regeneration on an equivalent level.
Authors: Teja Guda; John A Walker; Brian M Singleton; Jesus W Hernandez; Jun-Sik Son; Su-Gwan Kim; Daniel S Oh; Mark R Appleford; Joo L Ong; Joseph C Wenke Journal: Tissue Eng Part A Date: 2012-09-14 Impact factor: 3.845
Authors: Jin-Hyung Shim; Jung-Bo Huh; Ju Young Park; Young-Chan Jeon; Seong Soo Kang; Jong Young Kim; Jong-Won Rhie; Dong-Woo Cho Journal: Tissue Eng Part A Date: 2012-10-04 Impact factor: 3.845
Authors: Xavier Struillou; Mia Rakic; Zahi Badran; Laure Macquigneau; Caroline Colombeix; Paul Pilet; Christian Verner; Olivier Gauthier; Pierre Weiss; Assem Soueidan Journal: J Mater Sci Mater Med Date: 2013-08-03 Impact factor: 3.896
Authors: Daniel Rothamel; Marcel Benner; Tim Fienitz; Arndt Happe; Matthias Kreppel; Hans-Joachim Nickenig; Joachim E Zöller Journal: Head Face Med Date: 2014-03-27 Impact factor: 2.151