AIM: As bond strength of currently available adhesive systems in caries-affected teeth dentin on primary tooth dentin was not well known, the bond strength of two bonding systems (PQI and OptiBond Solo Plus) was evaluated on caries-affected and sound primary molar tooth dentin and observed the micromorphology of the adhesive-dentin interfaces. METHODS: By grinding both the sound (n = 30) and caries-affected (n = 30) approximal surfaces of teeth, flat dentin surfaces were obtained. The prepared surfaces were bonded with one of the each adhesive systems and a composite resin. After storing the bonded specimens in water at 37 degrees C for 24 h, the samples were sectioned and the bond strength of the adhesive systems was tested by the microshear test method. The data were statistically analysed. RESULTS: Microshear bond strengths of PQIgroup for caries-affected and sound primary tooth dentin were 9.43 +/- 2.44 (MPa) and 9.32 +/- 2.95 (MPa) (P > 0.05), respectively, and the bond strengths of OptiBond Solo Plus group for caries-affected and sound primary tooth dentin were 15.33 +/- 3.59 (MPa) and 11.96 +/- 2.30 (MPa) (P < 0.05), respectively. Micromorphological features between sound and caries-affected dentin were similar in both PQI and OptiBond Solo Plus groups. CONCLUSION: Both the adhesives showed significantly different bond strengths in caries-affected dentin but showed similar bond strengths in sound dentin.
RCT Entities:
AIM: As bond strength of currently available adhesive systems in caries-affected teeth dentin on primary tooth dentin was not well known, the bond strength of two bonding systems (PQI and OptiBond Solo Plus) was evaluated on caries-affected and sound primary molar tooth dentin and observed the micromorphology of the adhesive-dentin interfaces. METHODS: By grinding both the sound (n = 30) and caries-affected (n = 30) approximal surfaces of teeth, flat dentin surfaces were obtained. The prepared surfaces were bonded with one of the each adhesive systems and a composite resin. After storing the bonded specimens in water at 37 degrees C for 24 h, the samples were sectioned and the bond strength of the adhesive systems was tested by the microshear test method. The data were statistically analysed. RESULTS: Microshear bond strengths of PQI group for caries-affected and sound primary tooth dentin were 9.43 +/- 2.44 (MPa) and 9.32 +/- 2.95 (MPa) (P > 0.05), respectively, and the bond strengths of OptiBond Solo Plus group for caries-affected and sound primary tooth dentin were 15.33 +/- 3.59 (MPa) and 11.96 +/- 2.30 (MPa) (P < 0.05), respectively. Micromorphological features between sound and caries-affected dentin were similar in both PQI and OptiBond Solo Plus groups. CONCLUSION: Both the adhesives showed significantly different bond strengths in caries-affected dentin but showed similar bond strengths in sound dentin.