Residual stress relaxation in the core of optical fiber by CO(2) laser irradiation.

We observed residual stress relaxation by CO(2) laser irradiation in the cores of optical fibers by direct stress measurement. It was demonstrated that the mechanical stress was fully relaxed by CO(2) laser irradiation and that the remaining stress in the core was thermal stress that was due to a mismatch of the thermal expansion coefficients of the fiber core and cladding. The net core stresses after relaxation were 17, 68, and 203 MPa in Ge-B-codoped fibers drawn at 0.53, 1.38, and 3.48 N, respectively. Changes in the refractive indices of the cores as a result of residual stress relaxation were also estimated.