PURPOSE: To evaluate the effect of CO2 laser treatment through topically applied amine fluoride solution on demineralised enamel. MATERIALS AND METHODS: Sixty extracted human molar crowns were selected and cut longitudinally into half. One half was subjected to a 10-day pH-cycling procedure to create caries-like lesions, whereas the other was left non-demineralised. The following treatments were randomly assigned (one treatment per tooth, on respective non-demineralised and demineralised matched specimens): exposure to a 1% amine fluoride solution for 15 s without irradiation (group I), irradiation for 15 s with a continuous-wave CO2 laser (group II), or laser-treatment for 15 s through the amine fluoride solution applied immediately beforehand (group III). Fluoride uptake (n = 30) and acid resistance (n = 30) were determined after treatment. Enamel surface alterations after laser irradiation were monitored using scanning electron microscopy. RESULTS: In groups I and III, an increased fluoride uptake was detected (p < or = 0.05). Laser irradiation through topical fluoride resulted in an increased acid resistance of sound and demineralised enamel specimens in deeper layers (p < or = 0.05). In addition, less surface alterations were observed in SEM examination of specimens irradiated through the amine fluoride solution compared with counterparts treated with laser only. CONCLUSIONS: CO2 laser light application through an amine fluoride solution may be instrumental in enhancing acid resistance of sound and demineralised enamel.
PURPOSE: To evaluate the effect of CO2 laser treatment through topically applied amine fluoride solution on demineralised enamel. MATERIALS AND METHODS: Sixty extracted human molar crowns were selected and cut longitudinally into half. One half was subjected to a 10-day pH-cycling procedure to create caries-like lesions, whereas the other was left non-demineralised. The following treatments were randomly assigned (one treatment per tooth, on respective non-demineralised and demineralised matched specimens): exposure to a 1% amine fluoride solution for 15 s without irradiation (group I), irradiation for 15 s with a continuous-wave CO2 laser (group II), or laser-treatment for 15 s through the amine fluoride solution applied immediately beforehand (group III). Fluoride uptake (n = 30) and acid resistance (n = 30) were determined after treatment. Enamel surface alterations after laser irradiation were monitored using scanning electron microscopy. RESULTS: In groups I and III, an increased fluoride uptake was detected (p < or = 0.05). Laser irradiation through topical fluoride resulted in an increased acid resistance of sound and demineralised enamel specimens in deeper layers (p < or = 0.05). In addition, less surface alterations were observed in SEM examination of specimens irradiated through the amine fluoride solution compared with counterparts treated with laser only. CONCLUSIONS:CO2 laser light application through an amine fluoride solution may be instrumental in enhancing acid resistance of sound and demineralised enamel.
Authors: Alberto González-Rodríguez; Juan de Dios López-González; Juan de Dios Luna del Castillo; Juan Villalba-Moreno Journal: Lasers Med Sci Date: 2010-04-27 Impact factor: 3.161