OBJECTIVE: The aim of this study was to verify the influence of endodontic sealers on the bond strength of an adhesive system and a resin cement used for carbon posts cementation. METHODS: Thirty extracted human premolars were instrumented and randomly divided into three groups according to the tested sealer: EndoFill, Sealapex, or EndoREZ. Specimens were stored at 37 degrees C. After 48 h, half of specimens were prepared to receive the post and the others after 7 days. The posts were cemented with Adper Single Bond/Rely X ARC and stored in distilled water at 37 degrees C for 7 days. After this period, the specimens were sectioned in three slices (coronal, middle, and apical). The push-out test was performed in a universal machine and the debonded area was examined in a stereomicroscope. RESULTS: Data were submitted ANOVA and Tukey test (alpha = 0.05). The EndoFill showed lower bond strength than other sealers (p < 0.01). The EndoREZ sealer was statistically greater than other groups for coronal and middle portions and similar for apical portion (p > 0.05). Coronal and middle portions showed the best results for all groups, mainly when the canal preparation was performed after 48 h (p < 0.01). Mixed failure occurs with more frequency (55.6%) followed by failure in adhesive-dentin interface (34.4%) and adhesive-post interface (10.0%). CONCLUSION: The use of EndoREZ sealer promoted higher bond strength in root coronal and middle portions when carbon post was fixed with a resin cement. (c) 2007 Wiley Periodicals, Inc.
OBJECTIVE: The aim of this study was to verify the influence of endodontic sealers on the bond strength of an adhesive system and a resin cement used for carbon posts cementation. METHODS: Thirty extracted human premolars were instrumented and randomly divided into three groups according to the tested sealer: EndoFill, Sealapex, or EndoREZ. Specimens were stored at 37 degrees C. After 48 h, half of specimens were prepared to receive the post and the others after 7 days. The posts were cemented with Adper Single Bond/Rely X ARC and stored in distilled water at 37 degrees C for 7 days. After this period, the specimens were sectioned in three slices (coronal, middle, and apical). The push-out test was performed in a universal machine and the debonded area was examined in a stereomicroscope. RESULTS: Data were submitted ANOVA and Tukey test (alpha = 0.05). The EndoFill showed lower bond strength than other sealers (p < 0.01). The EndoREZ sealer was statistically greater than other groups for coronal and middle portions and similar for apical portion (p > 0.05). Coronal and middle portions showed the best results for all groups, mainly when the canal preparation was performed after 48 h (p < 0.01). Mixed failure occurs with more frequency (55.6%) followed by failure in adhesive-dentin interface (34.4%) and adhesive-post interface (10.0%). CONCLUSION: The use of EndoREZ sealer promoted higher bond strength in root coronal and middle portions when carbon post was fixed with a resin cement. (c) 2007 Wiley Periodicals, Inc.