Synthesis, crystal structure, and properties of two modifications of MgB(12)C(2).

Single crystals of two modifications of the new magnesium boride carbide MgB(12)C(2) were synthesized from the elements in a metallic melt by using tantalum ampoules. Crystals were characterized by single-crystal X-ray diffraction and electron microprobe analysis (energy-dispersive (EDX) and wavelength-dispersive (WDX) X-ray spectroscopy). Orthorhombic MgB(12)C(2) is formed in a Cu/Mg melt at 1873 K. The crystal structure of o-MgB(12)C(2) (Imma, Z=4, a=5.6133(10), b=9.828(2), c=7.9329(15) A, 574 reflections, 42 variables, R(1)(F)=0.0208, wR(2)(I)=0.0540) consists of a hexagonal primitive array of B(12) icosahedra with Mg atoms and C(2) units in trigonal-prismatic voids. Each icosahedron has six exohedral B--B and six B--C bonds. Carbon is tetrahedrally coordinated by three boron atoms and one carbon atom with a remarkably long C--C distance of 1.727 A. Monoclinic MgB(12)C(2) is formed in an Al/Mg melt at 1573 K. The structure of m-MgB(12)C(2) (C2/c, Z=4, a=7.2736(11), b=8.7768(13), c=7.2817(11) A, beta=105.33(3) degrees , 1585 reflections, 71 variables, R(1)(F)=0.0228, wR(2)(I)=0.0610) may be described as a distorted cubic close arrangement of B(12) icosahedra. Tetrahedral voids are filled by C atoms and octahedral voids are occupied by Mg atoms. The icosahedra are interconnected by four exohedral B--B bonds to linear chains and by eight interstitial C atoms to form a three-dimensional covalent network. Both compounds fulfill the electron-counting rules of Wade and Longuet-Higgins.