Hydroxyapatite/titania sol-gel coatings on titanium-zirconium alloy for biomedical applications.

A simple sol-gel method was developed for hydroxyapatite/titania (HA/TiO(2)) coatings on non-toxic titanium-zirconium (TiZr) alloy for biomedical applications. The HA/TiO(2)-coated TiZr alloy displayed excellent bioactivity when soaked in a simulated body fluid (SBF) for an appropriate period. Differential scanning calorimetry, thermogravimetric analysis, X-ray diffraction and scanning electron microscopy-energy dispersive spectrometry were used to characterize the phase transformations and the surface structures and to assess the in vitro tests. The HA/TiO(2) layers were spin-coated on the surface of TiZr alloy at a speed of 3000rpm for 15s, followed by a heat treatment at 600 degrees C for 20min in an argon atmosphere sequentially. The TiO(2) layer exhibited a cracked surface and an anatase structure and the HA layer displayed a uniform dense structure. Both the TiO(2) and HA layers were 25microm thick, and the total thickness of the HA/TiO(2) coatings was 50microm. The TiZr alloy after the above HA/TiO(2) coatings displayed excellent bone-like apatite-forming ability when soaked in SBF and can be anticipated to be a promising load-bearing implant material.