OBJECTIVE: The purpose of this study was to investigate the influence of Nd:YAG on microtensile bond strength (microTBS) of different adhesive systems for human dentin. BACKGROUND DATA: Lasers have been widely used in dentistry. New adhesive systems with different chemical compositions are introduced every year, and it is important to investigate the bonding of new adhesive systems to dentin irradiated with laser. METHODS: The occlusal surfaces of third molars were removed to obtain flat dentin surfaces. The teeth were randomly divided into six groups. Each adhesive system was applied, according to manufacturers' instructions, to surface dentine with and without Nd:YAG laser irradiation (0.9 W, 15 Hz, 60 mJ per pulse). A block of composite resin was built over the adhesive layer. The specimens were sectioned to obtain 0.70 x 0.70 mm of transversal section. Twenty test specimens were selected for each group, and were then submitted to microTBS on a universal testing machine. RESULTS: According to Student's t-test, for Single Bond, there was no statistically significant difference without (49.32 MPa) and with (47.34 MPa) laser application (p = 0.60). For the Tyrian SPE/One Step Plus, microTBS value with laser (27.09 MPa) was statistically higher than without laser (19.13 MPa), as well as for Adper Prompt L-Pop (22.85 and 13.78 Mpa; p < or = 0.01). CONCLUSION: The application of Nd:YAG laser to dentin provided an increase in the bond strength values for the Tyrian SPE/One Step Plus and Adper Prompt L-Pop adhesive systems, but did not influence the bond strength values of the Single Bond adhesive system.
OBJECTIVE: The purpose of this study was to investigate the influence of Nd:YAG on microtensile bond strength (microTBS) of different adhesive systems for human dentin. BACKGROUND DATA: Lasers have been widely used in dentistry. New adhesive systems with different chemical compositions are introduced every year, and it is important to investigate the bonding of new adhesive systems to dentin irradiated with laser. METHODS: The occlusal surfaces of third molars were removed to obtain flat dentin surfaces. The teeth were randomly divided into six groups. Each adhesive system was applied, according to manufacturers' instructions, to surface dentine with and without Nd:YAG laser irradiation (0.9 W, 15 Hz, 60 mJ per pulse). A block of composite resin was built over the adhesive layer. The specimens were sectioned to obtain 0.70 x 0.70 mm of transversal section. Twenty test specimens were selected for each group, and were then submitted to microTBS on a universal testing machine. RESULTS: According to Student's t-test, for Single Bond, there was no statistically significant difference without (49.32 MPa) and with (47.34 MPa) laser application (p = 0.60). For the Tyrian SPE/One Step Plus, microTBS value with laser (27.09 MPa) was statistically higher than without laser (19.13 MPa), as well as for Adper Prompt L-Pop (22.85 and 13.78 Mpa; p < or = 0.01). CONCLUSION: The application of Nd:YAG laser to dentin provided an increase in the bond strength values for the Tyrian SPE/One Step Plus and Adper Prompt L-Pop adhesive systems, but did not influence the bond strength values of the Single Bond adhesive system.