Irini D Sideridou1, Maria M Karabela, Dimitris N Bikiaris. 1. Laboratory of Organic Chemical Technology, Department of Chemistry, Aristotle University of Thessaloniki, GR-54 124 Thessaloniki, Greece. siderid@chem.auth.gr
Abstract
OBJECTIVE: To study the aging of neat resins, prepared from bis-GMA, UDMA, D(3)MA or a mixture of bis-GMA/UDMA/D(3)MA (65/20/15 w/w/w), in water or 75% (v/v) ethanol/water 37 degrees C. Also the study of aging of Heliomolar RO, which is a radiopaque, microfilled, light cured composite, the resin matrix of which is the copolymer of bis-GMA/UDMA/D(3)MA (65/20/15 w/w/w). METHODS: Samples of neat resins and Heliomolar RO prepared by light curing were immersed in water or 75% (v/v) ethanol/water 37 degrees C, for 1, 7 or 30 days. Then the flexural and tensile strength were determined. The fractured surface of samples after the flexural tests was observed by scanning electron microscopy. RESULTS: Bis-GMA and copolymer resin did not showed any significant change in mechanical properties after immersion in water or 75% (v/v) ethanol/water 37 degrees C, for 30 days. On the contrary UDMA, D(3)MA and the composite Heliomolar RO showed a significant decrease. SIGNIFICANCE: The results obtained showed that the effect of aging in water or ethanol/water solution on mechanical properties of a light cured dimethacrylate resin depends on the chemical structure of resin. In the case of resin composite this effect depends on the filler-matrix bond strength.
OBJECTIVE: To study the aging of neat resins, prepared from bis-GMA, UDMA, D(3)MA or a mixture of bis-GMA/UDMA/D(3)MA (65/20/15 w/w/w), in water or 75% (v/v) ethanol/water 37 degrees C. Also the study of aging of Heliomolar RO, which is a radiopaque, microfilled, light cured composite, the resin matrix of which is the copolymer of bis-GMA/UDMA/D(3)MA (65/20/15 w/w/w). METHODS: Samples of neat resins and Heliomolar RO prepared by light curing were immersed in water or 75% (v/v) ethanol/water 37 degrees C, for 1, 7 or 30 days. Then the flexural and tensile strength were determined. The fractured surface of samples after the flexural tests was observed by scanning electron microscopy. RESULTS:Bis-GMA and copolymer resin did not showed any significant change in mechanical properties after immersion in water or 75% (v/v) ethanol/water 37 degrees C, for 30 days. On the contrary UDMA, D(3)MA and the composite Heliomolar RO showed a significant decrease. SIGNIFICANCE: The results obtained showed that the effect of aging in water or ethanol/water solution on mechanical properties of a light cured dimethacrylate resin depends on the chemical structure of resin. In the case of resin composite this effect depends on the filler-matrix bond strength.
Authors: Jordan E Boulden; Neil B Cramer; Kathleen M Schreck; Charles L Couch; Cora Bracho-Troconis; Jeffrey W Stansbury; Christopher N Bowman Journal: Dent Mater Date: 2010-11-30 Impact factor: 5.304
Authors: Sebastian Hahnel; Anne Henrich; Martin Rosentritt; Gerhard Handel; Ralf Bürgers Journal: J Mater Sci Mater Med Date: 2009-10-15 Impact factor: 3.896
Authors: Ellen Elisabeth Jansen; Hendrik Meyer-Lueckel; Marcella Esteves-Oliveira; Richard Johannes Wierichs Journal: Clin Oral Investig Date: 2020-12-14 Impact factor: 3.573