Macrophage uptake of core-shell nanoparticles surface modified with poly(ethylene glycol).

The in vitro uptake of core-shell nanoparticles encapsulated in a bio-macromolecular nanoshell assembled from multilayered polyelectrolytes was studied. Sulfate modified fluorescent polystyrene nanobeads (diameter 200 nm) were used as a solid core upon which charged multilayers of poly-l-lysine, chitosan, and heparin sulfate are electrostatically deposited utilizing a layer-by-layer (LbL) self-assembly process. The nanoshell composed of the multilayered polyelectrolytes was modified with poly(ethylene glycol) (PEG) of varying molecular weights (either MW 2000, 5000, or 20 000 Da) to form a hydrophilic and long-circulating nanoparticle. The assembly of the nanoshell was confirmed by zeta potential, transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). The reversal in charge upon the deposition of alternating polyelectrolytes was observed by zeta potential measurements. The nanometer thickness of the nanoshell was confirmed by TEM. The presence of the (C-C-O)(n)() backbone in PEG at the surface of the nanoshell was confirmed by the increase in (C-O,N) peak area concentrations compared to (C-C) peak area, and these results were gathered from XPS. In vitro studies between suspension macrophages and core-shell nanoparticles were performed to determine how the hydrophilicity and the charge on the nanoshell can promote or reduce uptake. Results showed that after 24 h uptake was decreased 3-fold when PEGs of 2000 and 20 000 Da were chemisorbed to the nanoshell, as opposed to a nanoshell with either a positive or highly negative charge. Confocal microscopy aided in verifying that core-shell nanoparticles were internalized within the cell cytoplasm and were not attached to the cell surface. Protein adhesion studies with bovine serum albumin were performed to determine the relationship between surface charge and opsonization of core-shell nanoparticles. It was found that a hydrophilic surface with a low negative charge reduced protein adsorption and uptake. The in vitro uptake of macrophages and protein adsorption onto core-shell nanoparticles formed using layer-by-layer assembly has not been previously studied.