STATEMENT OF PROBLEM: Clinicians must be aware of the bonding effectiveness of auto- and dual- polymerizing adhesive systems before choosing the material and technique of cementing inlay/onlays to dentin. An inadequate choice may compromise the success of indirect restorations. PURPOSE: This study compared the microtensile bond strength (MTBS) of indirect composite resin bonded to dentin by light-activated, autopolymerizing, and dual-polymerizing adhesive systems. MATERIAL AND METHODS: Occlusal dentin surfaces of 36 human third molars were exposed and flattened. Teeth were assigned to 1 of the following 6 groups (n=6) of adhesive luting systems: 2 dual-polymerizing systems (Scotchbond Multipurpose Plus/Rely X [SBMP] and Prime & Bond NT Dual Cure/Enforce [PBDC]); 1 autopolymerizing system (ED Primer/Panavia F [EDP]); and 3 light-activated systems (control groups) (Adper Single Bond/Rely X [SB], Prime & Bond NT/Enforce [PB], and Clearfil SE Bond/Panavia F [CF]). The restorative materials were applied according to manufacturer's directions. A 2-mm-thick prepolymerized composite resin (Clearfil APX) disc was cemented with the resin cements on the bonded dentin. Teeth were stored in water at 37 degrees C for 24 hours. Afterwards, teeth were sectioned both mesial-distally and buccal-lingually to obtain multiple bonded beam specimens with 0.8 mm(2) of cross-sectional area. Each specimen was tested in tension at a crosshead speed of 0.5 mm/min until failure. Data (MPa) were analyzed by 1-way analysis of variance and the Tukey post hoc test (alpha=.05). Failure patterns of tested specimens were analyzed using scanning electron microscopy. RESULTS: Mean MTBS values (MPa) for experimental groups were as follows: SBMP, 32.89 +/- 3.26(a); SB, 26.74 +/- 7.45(ab); PB, 26.11 +/- 4.48(ab); CF, 25.30 +/- 6.42(ab); EDP, 16.82 +/- 5.53(bc); PBDC, 11.20 +/- 5.89(c) (P<.001). Groups with similar lowercase letters were not significantly different. Failure pattern of fractured specimens varied according to the polymerization mode. CONCLUSION: The autopolymerizing system and one of the dual-polymerizing systems were as effective as the light-activated systems in bonding indirect composite restorations to dentin.
STATEMENT OF PROBLEM: Clinicians must be aware of the bonding effectiveness of auto- and dual- polymerizing adhesive systems before choosing the material and technique of cementing inlay/onlays to dentin. An inadequate choice may compromise the success of indirect restorations. PURPOSE: This study compared the microtensile bond strength (MTBS) of indirect composite resin bonded to dentin by light-activated, autopolymerizing, and dual-polymerizing adhesive systems. MATERIAL AND METHODS: Occlusal dentin surfaces of 36 human third molars were exposed and flattened. Teeth were assigned to 1 of the following 6 groups (n=6) of adhesive luting systems: 2 dual-polymerizing systems (Scotchbond Multipurpose Plus/Rely X [SBMP] and Prime & Bond NT Dual Cure/Enforce [PBDC]); 1 autopolymerizing system (ED Primer/Panavia F [EDP]); and 3 light-activated systems (control groups) (Adper Single Bond/Rely X [SB], Prime & Bond NT/Enforce [PB], and Clearfil SE Bond/Panavia F [CF]). The restorative materials were applied according to manufacturer's directions. A 2-mm-thick prepolymerized composite resin (Clearfil APX) disc was cemented with the resin cements on the bonded dentin. Teeth were stored in water at 37 degrees C for 24 hours. Afterwards, teeth were sectioned both mesial-distally and buccal-lingually to obtain multiple bonded beam specimens with 0.8 mm(2) of cross-sectional area. Each specimen was tested in tension at a crosshead speed of 0.5 mm/min until failure. Data (MPa) were analyzed by 1-way analysis of variance and the Tukey post hoc test (alpha=.05). Failure patterns of tested specimens were analyzed using scanning electron microscopy. RESULTS: Mean MTBS values (MPa) for experimental groups were as follows: SBMP, 32.89 +/- 3.26(a); SB, 26.74 +/- 7.45(ab); PB, 26.11 +/- 4.48(ab); CF, 25.30 +/- 6.42(ab); EDP, 16.82 +/- 5.53(bc); PBDC, 11.20 +/- 5.89(c) (P<.001). Groups with similar lowercase letters were not significantly different. Failure pattern of fractured specimens varied according to the polymerization mode. CONCLUSION: The autopolymerizing system and one of the dual-polymerizing systems were as effective as the light-activated systems in bonding indirect composite restorations to dentin.