OBJECTIVE: To evaluate the effect of an in vitro challenge (NaOCl immersion) on microtensile bond strength (MTBS) of five adhesive systems to dentin. METHODS: Flat dentin surfaces from 40 molars were bonded with three total-etch adhesives (Single Bond, Prime&Bond NT and the experimental Prime&Bond XP), and two self-etching agents (Clearfil SE Bond and Etch&Prime 3.0). Composite build-ups were constructed with Tetric Ceram. Teeth were then sectioned into beams of 1.0 mm2 cross-sectional area. Half of the beams were immersed in 10% NaOCl aqueous solution for 5 h. Each beam was tested in tension in an Instron machine at 0.5 mm/min. Data were analyzed by 2-way ANOVA and multiple comparisons tests (p < 0.05). RESULTS: Clearfil SE Bond and Single Bond attained higher MTBS than the other three adhesives. Prime&Bond NT and Prime&Bond XP performed equally, and Etch&Prime resulted in the lowest MTBS. After NaOCl immersion, MTBS decreased in all groups. The highest MTBS values were obtained for Clearfil SE Bond and Prime&Bond XP. Scaning electron microscopy observation of debonded sticks evidenced dissolution and microstructural alterations of intertubular dentin, except when Clearfil SE Bond was used. CONCLUSIONS: Resin-dentin bonds are prone to chemical degradation. The extent of the resin degradation is adhesive system specific. Chemical degradation of the nonresin infiltrated collagen fibers does also exist in total-etch adhesives. Both processes may reduce long-term resin-dentin bond strength. (c) 2005 Wiley Periodicals, Inc.
OBJECTIVE: To evaluate the effect of an in vitro challenge (NaOCl immersion) on microtensile bond strength (MTBS) of five adhesive systems to dentin. METHODS: Flat dentin surfaces from 40 molars were bonded with three total-etch adhesives (Single Bond, Prime&Bond NT and the experimental Prime&Bond XP), and two self-etching agents (Clearfil SE Bond and Etch&Prime 3.0). Composite build-ups were constructed with Tetric Ceram. Teeth were then sectioned into beams of 1.0 mm2 cross-sectional area. Half of the beams were immersed in 10% NaOCl aqueous solution for 5 h. Each beam was tested in tension in an Instron machine at 0.5 mm/min. Data were analyzed by 2-way ANOVA and multiple comparisons tests (p < 0.05). RESULTS: Clearfil SE Bond and Single Bond attained higher MTBS than the other three adhesives. Prime&Bond NT and Prime&Bond XP performed equally, and Etch&Prime resulted in the lowest MTBS. After NaOCl immersion, MTBS decreased in all groups. The highest MTBS values were obtained for Clearfil SE Bond and Prime&Bond XP. Scaning electron microscopy observation of debonded sticks evidenced dissolution and microstructural alterations of intertubular dentin, except when Clearfil SE Bond was used. CONCLUSIONS: Resin-dentin bonds are prone to chemical degradation. The extent of the resin degradation is adhesive system specific. Chemical degradation of the nonresin infiltrated collagen fibers does also exist in total-etch adhesives. Both processes may reduce long-term resin-dentin bond strength. (c) 2005 Wiley Periodicals, Inc.
Authors: Manuel Toledano; Raquel Osorio; Estrella Osorio; Fátima S Aguilera; Monica Yamauti; David H Pashley; Franklin Tay Journal: J Mater Sci Mater Med Date: 2007-06-14 Impact factor: 3.896
Authors: Raquel Osorio; Estrella Osorio; Fátima S Aguilera; Franklin R Tay; Alexandra Pinto; Manuel Toledano Journal: Odontology Date: 2010-07-23 Impact factor: 2.634
Authors: Salvatore Sauro; Manuel Toledano; Fatima Sánchez Aguilera; Francesco Mannocci; David H Pashley; Franklin R Tay; Timothy F Watson; Raquel Osorio Journal: Dent Mater Date: 2010-01-13 Impact factor: 5.304