Effect of KOH activation on the formation of oxygen structure in activated carbons synthesized from polymeric precursor.

In this work, the influence of KOH activation on the surface chemistry of activated carbons (ACs) synthesized from polystyrene-based cation exchangeable resin (PSI) has been investigated. The surface chemistry of ACs has been characterized by using Fourier transformed infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), pH measurement, and Boehm's titration method. As a result, PSI can be successfully converted into ACs with high porosities. The total oxygen content on the ACs studied increases with increasing the KOH-to-PSI ratio. FT-IR and XPS analyses show that the resulting carbons possess a number of oxygen surface functional groups, such as carbonyl, quinone, phenol, ether, and carboxylic acid groups. The highest oxygen content and acid value are observed at a KOH-to-PSI ratio of 4 (KPS-4). However, its pH and surface basicity are higher than those of a KOH-to-PSI ratio of 2 (KPS-2), indicating the formation of basic species, such as quinone and pyrone groups. Although the oxygen-containing groups with basic character exist in the resulting carbons, all the samples are still acidic in character.