Size-controlled hydroxyapatite nanoparticles as self-organized organic-inorganic composite materials.

This paper presents some results concerning the size-controlled hydroxyapatite nanoparticles obtained in aqueous media in a biopolymer matrix from soluble precursors salts. Taking the inspiration from nature, where composite materials made of a polymer matrix and inorganic fillers are often found, e.g. bone, shell of crustaceans, shell of eggs, etc., the feasibility on making composite materials containing chitosan and nanosized hydroxyapatite was investigated. A stepwise co-precipitation approach was used to obtain different types of composites by means of different ratio between components. The synthesis of hydroxyapatite was carried out in the chitosan matrix from calcium chloride and sodium dihydrogenphosphate in alkaline solutions at moderate pH of 10-11 for 24 h. Our research is focused on studying and understanding the structure of this class of composites, aiming at the development of novel materials, controlled at the nanolevel scale. The X-ray diffraction technique was employed in order to study the kinetic of hydroxyapatite formation in the chitosan matrix as well as to determine the HAp crystallite sizes in the composite samples. The hydroxyapatite synthesized using this route was found to be nano-sized (15-50 nm). Moreover, applying an original approach to analyze the (002) XRD diffraction peak profile of hydroxyapatite by using a sum of two Gauss functions, the bimodal distribution of nanosized hydroxyapatite within the chitosan matrix was revealed. Two types of size distribution domains such as cluster-like (between 200 and 400 nm), which are the habitat of ''small'' hydroxyapatite nanocrystallites and scattered-like, which are the habitat of ''large'' hydroxyapatite nanocrystallites was probed by TEM and CSLM. The structural features of composites suggest that self-assembly processes might be involved. The composites contain nanosized hydroxyapatite with structural features close to those of biological apatites that make them attractive for bone tissue engineering applications.