STATEMENT OF PROBLEM: Ceramic surface treatment is crucial for bonding to resin. High crystalline ceramics are poorly conditioned using traditional procedures. PURPOSE: The purpose of this study was to evaluate the effect of silica coating on a densely sintered alumina ceramic relative to its bond strength to composite, using a resin luting agent. Material and methods Blocks (6 x 6 x 5 mm) of ceramic and composite were made. The ceramic (Procera AllCeram) surfaces were polished, and the blocks were divided into 3 groups (n = 5): SB, airborne-particle abrasion with 110-microm Al 2 O 3 ; RS, silica coating using Rocatec System; and CS, silica coating using CoJet System. The treated ceramic blocks were luted to the composite (W3D Master) blocks using a resin luting agent (Panavia F). Specimens were stored in distilled water at 37 degrees C for 7 days and then cut in 2 axes, x and y, to obtain specimens with a bonding area of approximately 0.6 mm 2 (n = 30). The specimens were loaded to failure in tension in a universal testing machine, and data were statistically analyzed using a randomized complete block design analysis of variance and Tukey's test (alpha=.05). Fractured surfaces were examined using light microscopy and scanning electron microscopy to determine the type of failure. Energy-dispersive spectroscopy was used for surface compositional analysis. RESULTS:Mean bond strength values (MPa) of Groups RS (17.1 +/- 3.9) ( P =.00015) and CS (18.5 +/- 4.7) ( P =.00012) were significantly higher than the values of Group SB (12.7 +/- 2.6). There was no statistical difference between Groups RS and CS. All failures occurred at the adhesive zone. CONCLUSION: Tribochemical silica coating systems increased the tensile bond strength values between Panavia F and Procera AllCeram ceramic.
RCT Entities:
STATEMENT OF PROBLEM: Ceramic surface treatment is crucial for bonding to resin. High crystalline ceramics are poorly conditioned using traditional procedures. PURPOSE: The purpose of this study was to evaluate the effect of silica coating on a densely sintered alumina ceramic relative to its bond strength to composite, using a resin luting agent. Material and methods Blocks (6 x 6 x 5 mm) of ceramic and composite were made. The ceramic (Procera AllCeram) surfaces were polished, and the blocks were divided into 3 groups (n = 5): SB, airborne-particle abrasion with 110-microm Al 2 O 3 ; RS, silica coating using Rocatec System; and CS, silica coating using CoJet System. The treated ceramic blocks were luted to the composite (W3D Master) blocks using a resin luting agent (Panavia F). Specimens were stored in distilled water at 37 degrees C for 7 days and then cut in 2 axes, x and y, to obtain specimens with a bonding area of approximately 0.6 mm 2 (n = 30). The specimens were loaded to failure in tension in a universal testing machine, and data were statistically analyzed using a randomized complete block design analysis of variance and Tukey's test (alpha=.05). Fractured surfaces were examined using light microscopy and scanning electron microscopy to determine the type of failure. Energy-dispersive spectroscopy was used for surface compositional analysis. RESULTS: Mean bond strength values (MPa) of Groups RS (17.1 +/- 3.9) ( P =.00015) and CS (18.5 +/- 4.7) ( P =.00012) were significantly higher than the values of Group SB (12.7 +/- 2.6). There was no statistical difference between Groups RS and CS. All failures occurred at the adhesive zone. CONCLUSION: Tribochemical silica coating systems increased the tensile bond strength values between Panavia F and Procera AllCeram ceramic.
Authors: Carlos de Paula Eduardo; Marina Stella Bello-Silva; Simone Gonçalves Moretto; Paulo Francisco Cesar; Patricia Moreira de Freitas Journal: Lasers Med Sci Date: 2010-08-25 Impact factor: 3.161
Authors: Karen Müller Ramalho; Patrícia Moreira de Freitas; Ana Cecília Correa-Aranha; Marina Stella Bello-Silva; Roberta Marques da Graça Lopes; Carlos de Paula Eduardo Journal: Case Rep Dent Date: 2014-07-23
Authors: Mohamed A Qudaih; Salah A Yousief; Mahmoud N M Allabban; Ali Abkar Mohammed Nejri; Ahmed Mohamed Elmarakby Journal: Clin Cosmet Investig Dent Date: 2020-03-30