Surface-tunable photoluminescence from block copolymer-stabilized cadmium sulfide quantum dots.

The static and time-resolved photoluminescence properties of polystyrene-b-poly(acrylic acid) (PS-b-PAA)-stabilized cadmium sulfide quantum dots (CdS QDs) have been characterized for the first time, demonstrating tunable emission spectra and quantum yields via different chemical treatments of the PAA layer. Samples with the PAA layer in its cadmium carboxylate form showed more-intense band-edge emission and relatively high quantum yields compared with samples in which the PAA layer was in its acid form. This activation effect is explained in terms of passivation of trap sites on the QD surface by specific interactions between the QD and the cadmium-neutralized PAA layer. Lifetimes of band-edge and trap state emission for the various samples ranged from 40 to 61 ns and 244 to 360 ns, respectively. Impressive long-term stability was also shown for a sample of cadmium-neutralized PS-b-PAA-stabilized QDs dispersed in toluene, which maintained 90% of its photoluminescence over 57 days aging under ambient conditions. It is also shown that Cd2+ activation of photoluminescence does not occur when Mg2+ ions are added to similar QD solutions, indicating potential of these block copolymer-stabilized QDs as Cd2+-selective sensors. Irrespective of chemical treatment of the PAA layer, the external PS brush layer effectively stabilized all samples in various organic solvents, resulting in clear CdS colloids with no observed precipitation over several months. Dynamic light scattering and gel permeation chromatography revealed differences in the aggregation numbers and hydrodynamic radii of colloidal QDs for different treatments of the PAA layer, attributed to the lower solubility of the poly(cadmium acrylate) blocks compared to the PAA blocks in the acid form. Finally, it was demonstrated that the PS-b-PAA-stabilized QDs could be well dispersed in PS homopolymer, producing optically transparent photoluminescent films which retained the emission features of the colloidal QDs. Stable and surface-tunable optical properties via the PAA layer and polymer solubility and processability via the PS layer make these PS-b-PAA-stabilized CdS QDs exciting "building blocks" for the bottom-up assembly of functional hierarchical materials for photonics, sensors, and bio-labeling applications.