UNLABELLED: The aim of this study was to examine the morphology of the hybrid layer (HL) of bonded water-stored specimens after different chemical pre-treatments of dentin. MATERIALS AND METHODS: Twenty-seven recently extracted human molars were selected. Fifty-four dentin disks in middle/deep dentin were obtained with a slow speed saw with a diamond-impregnated disk under water lubrication. Smear layers were created with 180 grit silicon carbide under running water for 1 min. Different pre-treatments of dentin were: Group (1) no treatment; Group (2) 35% H3PO4 etch for 15 s followed by 10% glutaraldehyde for 120 s; Group (3) 37% H3PO4 etch for 15 s followed by 5% NaOCl for 120 s. Three dentin bonding agents (DBAs), Prime and Bond NT (P and B), AdmiraBond (AB), and Clearfil SE Bond (SEB) were applied in association with a resin composite following the manufacturers' directions. Each specimen was then longitudinally sectioned and polished with wet SiC papers (up to #4000 grit). Impressions of the polished dentin were immediately taken with a silicone impression material. Bonded specimens were then stored for 3 or 12 h in deionized water. Further impressions of stored specimens were taken after air-drying of specimens for 10 s. Positive replicas were obtained using a polyether impression material. All the replicas and the original specimens were inspected by SEM. RESULTS: A line of droplets (0.5-4 microm in diameter) was observed along the region of the adhesive-HL junction in all replicas of specimens stored in water, except in group 3, when P and B and AB were used. When SEB was used in each group the droplet were found in all groups except the zone of droplets was thinner. No differences in droplets dimensions were seen between 3 or 12 h water storage, or between the different dentin treatments. CONCLUSIONS: The replica procedure used in this study was able to detect water trapped in the adhesive-HL region that was released during the setting of the impression material. The droplets observed in this region support the hypothesis that there can be bidirectional water movement within the adhesive-HL complex.
UNLABELLED: The aim of this study was to examine the morphology of the hybrid layer (HL) of bonded water-stored specimens after different chemical pre-treatments of dentin. MATERIALS AND METHODS: Twenty-seven recently extracted human molars were selected. Fifty-four dentin disks in middle/deep dentin were obtained with a slow speed saw with a diamond-impregnated disk under water lubrication. Smear layers were created with 180 grit silicon carbide under running water for 1 min. Different pre-treatments of dentin were: Group (1) no treatment; Group (2) 35% H3PO4etch for 15 s followed by 10% glutaraldehyde for 120 s; Group (3) 37% H3PO4etch for 15 s followed by 5% NaOCl for 120 s. Three dentin bonding agents (DBAs), Prime and Bond NT (P and B), AdmiraBond (AB), and Clearfil SE Bond (SEB) were applied in association with a resin composite following the manufacturers' directions. Each specimen was then longitudinally sectioned and polished with wet SiC papers (up to #4000 grit). Impressions of the polished dentin were immediately taken with a silicone impression material. Bonded specimens were then stored for 3 or 12 h in deionized water. Further impressions of stored specimens were taken after air-drying of specimens for 10 s. Positive replicas were obtained using a polyether impression material. All the replicas and the original specimens were inspected by SEM. RESULTS: A line of droplets (0.5-4 microm in diameter) was observed along the region of the adhesive-HL junction in all replicas of specimens stored in water, except in group 3, when P and B and AB were used. When SEB was used in each group the droplet were found in all groups except the zone of droplets was thinner. No differences in droplets dimensions were seen between 3 or 12 h water storage, or between the different dentin treatments. CONCLUSIONS: The replica procedure used in this study was able to detect water trapped in the adhesive-HL region that was released during the setting of the impression material. The droplets observed in this region support the hypothesis that there can be bidirectional water movement within the adhesive-HL complex.
Authors: Carlo Prati; Stefano Chersoni; Giovanni Luca Acquaviva; Lorenzo Breschi; Pietro Suppa; Franklin R Tay; David H Pashley Journal: Clin Oral Investig Date: 2005-01-21 Impact factor: 3.573
Authors: Juliana Malacarne-Zanon; David H Pashley; Kelli A Agee; Stephen Foulger; Marcelo Corrêa Alves; Lorenzo Breschi; Milena Cadenaro; Fernanda P Garcia; Marcela R Carrilho Journal: Dent Mater Date: 2009-07-09 Impact factor: 5.304
Authors: Juliana Malacarne-Zanon; Safira M de Andrade E Silva; Linda Wang; Mario F de Goes; Adriano Luis Martins; Eliene O Narvaes-Romani; Andrea Anido-Anido; Marcela R O Carrilho Journal: Eur J Dent Date: 2010-10
Authors: Marcela R Carrilho; Franklin R Tay; Adam M Donnelly; Kelli A Agee; Ricardo M Carvalho; Keiichi Hosaka; Alessandra Reis; Alessandro D Loguercio; David H Pashley Journal: J Biomed Mater Res B Appl Biomater Date: 2009-02 Impact factor: 3.368
Authors: Larissa Sgarbosa de Araújo Matuda; Giselle Maria Marchi; Thaiane Rodrigues Aguiar; Ariene Arcas Leme; Gláucia M B Ambrosano; Ana Karina Bedran-Russo Journal: Dent Mater Date: 2016-04-08 Impact factor: 5.304