Synthesis, characterization, and adsorption properties of nanocrystalline ZSM-5.

Nanocrystalline ZSM-5 with a Si/Al ratio of 20 was synthesized using clear solutions and a hydrothermal synthesis procedure. The resulting ZSM-5 materials were characterized by powder X-ray diffraction, scanning electron microscopy (SEM), nitrogen adsorption isotherms, solid-state nuclear magnetic resonance, and toluene adsorption. A commercial ZSM-5 sample was similarly characterized for comparison with the synthesized materials. The particle sizes of the synthesized ZSM-5 samples were calculated using the measured external surface areas and were determined to be 15 and 60 nm. SEM images indicated that the ZSM-5 samples consist of agglomerated and possibly intergrown particles. Toluene adsorption measurements showed that the ZSM-5 sample with a particle size of 15 nm adsorbed approximately 50% more toluene than the other ZSM-5 samples, most likely due to the adsorption of toluene on the external surface. For the toluene adsorbed on the internal zeolite surface, approximately one toluene molecule was adsorbed per channel intersection for each of the ZSM-5 samples.