Low temperature induced synthesis of TiN nanocrystals.

TiN nanocrystals were successfully prepared through the direct reaction between TiCl(4) and NaNH(2) induced at 300 degrees C. The yield based on Ti is approximately 80%. X-ray powder diffraction indicated that the product was cubic TiN with a lattice constant of a = 4.243 A. Transmission electron microscopy revealed that nanocrystalline TiN with a diameter of 10 nm or so and extremely long straight rods were synthesized. The possible formation mechanism was also proposed.