Importance of single or blended polymer types for controlled in vitro release and plasma levels of a somatostatin analogue entrapped in PLA/PLGA microspheres.

The aim of the work was to develop biodegradable microspheres for controlled delivery of the somatostatin analogue vapreotide and maintenance of sustained plasma levels over 2-4 weeks after a single injection in rats. Vapreotide was microencapsulated into end-group capped and uncapped low molecular weight poly(lactide) (PLA) and poly(lactide-co-glycolide) (PLGA) by spray-drying and coacervation. Microspheres were prepared from single and blended (1:1) polymer types. The microparticles were characterized for peptide loading, in vitro release and pharmocokinetics in rats. Spray-drying and coacervation produced microspheres in the size range of 1-15 and 10-70 microm, respectively, and with encapsulation efficiencies varying between 46% and 87%. In vitro release of vapreotide followed a regular pattern and lasted more than 4 weeks, time at which 40-80% of the total dose were released. Microspheres made of 14-kDa end-group uncapped PLGA50:50 or 1:1 blends of this polymer with 35 kDa end-group uncapped PLGA50:50 gave the best release profiles and yielded the most sustained plasma levels above a pre-defined 1 ng/ml over approximately 14 days. In vitro/in vivo correlation analyses showed for several microsphere formulations a linear correlation between the mean residence time in vivo and the mean dissolution time (r=0.958) and also between the amount released between 6 h and 14 days and the AUC(6h-14d) (r=0.932). For several other parameters or time periods, no in vitro/in vivo correlation was found. This study demonstrates that controlled release of the vapreotide is possible in vivo for a duration of a least 2 weeks when administered i.m. to rats. These results constitute a step forward towards a twice-a-month or once-a-month microsphere-formulation for the treatment of acromegaly and neuroendocrine tumors.