Formation of Zn(1-x)MnxS nanowires within mesoporous silica of different pore sizes.

Arrays of highly ordered Zn(1-x)MnxS quantum wires with x ranging from 0.01 to 0.3 and with lateral dimensions of 3, 6, and 9 nm were synthesized within mesoporous SiO2 host structures of the MCM-41 and SBA-15 type. The hexagonal symmetry of these arrays (space group p6m) and the high degree of order was confirmed by X-ray diffraction and transmission electron microscopy (TEM) studies. Physisorption measurements show the progressive filling of the pores of the SiO2 host structures, while TEM and Raman studies reveal the wire-like character of the incorporated Zn(1-x)MnxS nanostructures. X-ray absorption near-edge structure, extended X-ray absorption fine structure, photoluminescence excitation (PLE), and electron paramagnetic resonance studies confirm the good crystalline quality of the incorporated Zn(1-x)MnxS guest species and, in particular, that the Mn2+ ions are randomly distributed and are situated on tetrahedrally coordinated cation sites of the Zn(1-x)MnxS wires for all x up to 0.3. The amount of Mn2+ ions loosely bound to the surface of the Zn(1-x)MnxS nanowires is less than 4% of the total Mn content even for the 3 nm nanostructures up to the highest Mn content of x = 0.3. The effects of the reduction of the lateral dimensions on electronic properties of the diluted magnetic semiconductor were studied by PLE spectroscopy. Due to the quantum confinement of the excitons in the wires an increase of the direct band gap with decreasing particle size is observed.