F Picoli1, A Brugnera-Junior, P C Saquy, D M Z Guerisoli, J D Pecora. 1. Ribeirão Preto Dental School, University of São Paulo, Ribeirão Preto, and Camilo Castelo Branco University and Associação Paulista dos Cirurgiões-Dentistas, São Paulo, SP, Brazil.
Abstract
AIM: To evaluate the effect of 15% EDTAC solution and Er:YAG laser irradiation on the adhesiveness to dentine of root canal sealers containing calcium hydroxide. METHODOLOGY: The crowns of 60 maxillary human molars were ground until dentine was exposed. The teeth were divided into three groups of 20 teeth: group I, the dentine surface received no treatment; group II, 15% EDTAC solution was applied to the dentine; group III, the dentine received Er:YAG laser application (11 mm focal distance with perpendicular incidence to dentine surface; 4 Hz frequency; 200 mJ energy; 2.25 W potency; 62 J total energy; 1 min application time). Aluminium cylinders filled with the sealers, Sealer 26, Apexit, Sealapex and CRCS, were then applied to the treated surfaces. Adhesiveness was measured with a universal testing machine, with traction results given in MegaPascals (MPa). These results were submitted to anova tests. RESULTS: Statistical analysis showed significant differences (P < 0.01) amongst adhesiveness values of the sealers and treatments tested. Thus, sealers could be ranked in decreasing adhesiveness values: Sealer 26, CRCS, Apexit, Sealapex. Er:YAG laser irradiation and EDTAC solution application increased adhesiveness values only for Sealer 26 and Apexit. Laser irradiation was superior to EDTAC application only for Sealer 26 adhesiveness values. CONCLUSIONS: Er:YAG laser is as efficient as EDTAC solution in increasing adhesiveness of root canal sealers containing calcium hydroxide to human dentine.
RCT Entities:
AIM: To evaluate the effect of 15% EDTAC solution and Er:YAG laser irradiation on the adhesiveness to dentine of root canal sealers containing calcium hydroxide. METHODOLOGY: The crowns of 60 maxillary human molars were ground until dentine was exposed. The teeth were divided into three groups of 20 teeth: group I, the dentine surface received no treatment; group II, 15% EDTAC solution was applied to the dentine; group III, the dentine received Er:YAG laser application (11 mm focal distance with perpendicular incidence to dentine surface; 4 Hz frequency; 200 mJ energy; 2.25 W potency; 62 J total energy; 1 min application time). Aluminium cylinders filled with the sealers, Sealer 26, Apexit, Sealapex and CRCS, were then applied to the treated surfaces. Adhesiveness was measured with a universal testing machine, with traction results given in MegaPascals (MPa). These results were submitted to anova tests. RESULTS: Statistical analysis showed significant differences (P < 0.01) amongst adhesiveness values of the sealers and treatments tested. Thus, sealers could be ranked in decreasing adhesiveness values: Sealer 26, CRCS, Apexit, Sealapex. Er:YAG laser irradiation and EDTAC solution application increased adhesiveness values only for Sealer 26 and Apexit. Laser irradiation was superior to EDTAC application only for Sealer 26 adhesiveness values. CONCLUSIONS: Er:YAG laser is as efficient as EDTAC solution in increasing adhesiveness of root canal sealers containing calcium hydroxide to human dentine.
Authors: Tom Edgard Maria Vergauwen; Rafaël Michiels; Dries Torbeyns; Maarten Meire; Mieke De Bruyne; Roeland Jozef Gentil De Moor Journal: Int J Dent Date: 2014-02-19