BACKGROUND AND OBJECTIVES: The objective of this study was to determine whether a dissected aorta could be welded by a diode laser with a solder using an in vitro porcine aortic dissection model. STUDY DESIGN/ MATERIALS AND METHODS: Porcine aortic strips were dissected into two flaps and the dissected faces were immersed in a solution of indocyanine green. The two flaps were pressed at 0.2 kg/cm2 with contact between the two immersed faces. The pressed flaps were irradiated with a diode laser (810 nm) at intensities of 170-425 W/cm2 for 8 seconds. The welded flaps were studied by light microscopy and the adhesive strengths were measured. RESULTS: The irradiated flaps were successfully welded. The breaking stress, the maximum stress recorded in a stress-strain curve, increased with increase in irradiation intensity up to 396 W/cm2 (2.7 x 10(2) mmHg) and decreased when the intensity reached 425 W/cm2. In the specimen irradiated at 396 W/cm2, the welded faces showed continuous fusion of elastin layers, while some voids were seen between the welded faces in the specimen irradiated at 425 W/cm2. CONCLUSIONS: The dissected porcine aortas were successfully welded using a laser with solder. The results suggest that the welded aorta can bear physiological blood pressure. Copyright 2003 Wiley-Liss, Inc.
BACKGROUND AND OBJECTIVES: The objective of this study was to determine whether a dissected aorta could be welded by a diode laser with a solder using an in vitro porcine aortic dissection model. STUDY DESIGN/ MATERIALS AND METHODS: Porcine aortic strips were dissected into two flaps and the dissected faces were immersed in a solution of indocyanine green. The two flaps were pressed at 0.2 kg/cm2 with contact between the two immersed faces. The pressed flaps were irradiated with a diode laser (810 nm) at intensities of 170-425 W/cm2 for 8 seconds. The welded flaps were studied by light microscopy and the adhesive strengths were measured. RESULTS: The irradiated flaps were successfully welded. The breaking stress, the maximum stress recorded in a stress-strain curve, increased with increase in irradiation intensity up to 396 W/cm2 (2.7 x 10(2) mmHg) and decreased when the intensity reached 425 W/cm2. In the specimen irradiated at 396 W/cm2, the welded faces showed continuous fusion of elastin layers, while some voids were seen between the welded faces in the specimen irradiated at 425 W/cm2. CONCLUSIONS: The dissected porcine aortas were successfully welded using a laser with solder. The results suggest that the welded aorta can bear physiological blood pressure. Copyright 2003 Wiley-Liss, Inc.
Authors: Deogracias A G Reyes; Stuart I Brown; Lynda Cochrane; Luisa S Motta; Alfred Cuschieri Journal: Surg Endosc Date: 2012-07-07 Impact factor: 4.584