Preparation of aluminium-magnesium alloys and some valuable salts from used beverage cans.

The purpose of this work is to recover standard aluminium-magnesium alloy(s) and some valuable salts from used beverage cans (UBCs). The suggested method updated the current recycling technology by augmenting removal of the coating paint, decreasing magnesium loss during melting process and improving hydrochloric acid leaching of the formed slag. Iron impurity present in the leaching solution, was removed by oxidation using oxygen gas or hydrogen peroxide and filtered as goethite. Results obtained revealed that a mixture of methyl ethyl ketone/dimethyl formamide entirely removes the paint coating at room temperature. The process compares favorably to the current methods involving firing or swell peeling. The coating decomposes to titanium dioxide by heating at 750 degrees C for 30 min. Standard compositions of Al-Mg alloys are formulated using secondary magnesium. The extent of recovery (R) of these alloy(s) is a function of the melting time and temperature and type of the flux. The maximum (R) value amounts to 94.4%. Sodium borate/chloride mix decreases magnesium loss to a minimum. The extent of leaching valuable salts from the slag increases with increasing the molarity, stoichiometric ratio and leaching temperature of the acid used. Removal of iron is a function of the potential of the oxidation process. Stannous chloride has been recovered from the recovered and dried salts by distillation at 700-750 degrees C.